Item | Test method | Test data | Data unit |
Density | 0.955 | g/cm3 | |
MFR(190ºC,2.16KG) | 0.35 | g/10min | |
Tensile yield strength | 27 | Mpa | |
flexural modulus | 1370 | Mpa | |
Elongation at break | ≥600 | % | |
Brittle temperature | ≤-75 | ºC |
Item | Test method | Test data | Data unit |
Density | 0.955 | g/cm3 | |
MFR(190ºC,2.16KG) | 0.35 | g/10min | |
Tensile yield strength | 27 | Mpa | |
flexural modulus | 1370 | Mpa | |
Elongation at break | ≥600 | % | |
Brittle temperature | ≤-75 | ºC |
Item | Test method | Test data | Data unit |
Density | 0.955 | g/cm3 | |
MFR(190ºC,2.16KG) | 0.35 | g/10min | |
Tensile yield strength | 27 | Mpa | |
flexural modulus | 1370 | Mpa | |
Elongation at break | ≥600 | % | |
Brittle temperature | ≤-75 | ºC |
Item | Test method | Test data | Data unit |
Density | 0.955 | g/cm3 | |
MFR(190ºC,2.16KG) | 0.35 | g/10min | |
Tensile yield strength | 27 | Mpa | |
flexural modulus | 1370 | Mpa | |
Elongation at break | ≥600 | % | |
Brittle temperature | ≤-75 | ºC |