| Performance of the project | Test conditions [state] | test method | test data | data unit | |
basic performance | density | 0.9205~0.9245 | g/cm 3 | ||
| MFI | 1.7~2.3 | g/10min | |||
| physical properties | turbidity | ≤8 | ºC | ||
| thickness | 30 | μm | |||
| mechanical property | elongation at break | ≥500 | % | ||
| MDTensile strength | ≥18 | MPa | |||
| TDTensile strength | ≥17 | MPa | |||
| MDFracture elongation to break | ≥200 | % | |||
| Tensile strength | ≥9 | MPa | |||
| Shore hardness | ≥44 | ||||
| TD elongation at break | ≥450 | % | |||
| MD tear strength | ≥4.0 | CN/μm | |||
| impact strength | ≥2.0 | CN/μm | |||
| TD tear strength | vicat softening point | ≥3.0 | |||
thermal properties | vicat softening point | ≥90 | ºC | ||
| melting point | 106~111 | ºC | |||