Grinding Media Balls as Cement, Mining Mill Grinder

Grinding Media Balls as Cement, Mining Mill Grinder

Product Description
This product are featured by high density and hardness, low wear lost, corrosion-resistance etc. They are the perfect high-efficient grinding media for milling glaze/frit, pigment, ceramic materials, and various mine ore powder, they are using ceramics, cements, paints, refractories, inorganic mineral powders etc...

Appearance


Application
Applied for dry grinding , wet grinding ,mineral grinding ,  quartz grinding ,  lineston grinding ,  iron ore grinding , cement grinding , ceramics plants grinding , pigment grinding , mineral ore grinding , breaking platns .

Applied for ball mill,grinding machine , pot mill , librating mill , pebble mill , Attrition Mill,rod mill , grinding mill , grinding machine , ball grinding mill

Specification
Size:1mm, 3mm, 6mm, 9mm, 13mm, 16mm, 20mm, 25mm, 30mm , 40mm, 50mm, 60mm, 70mm,95mm

Techinical data
1: 92%  Alumina content series
A) Al2O3 ≥ 92%
B) Water absorption <0.01%
C) Bulk density ≥ 3.63 g/cm3
D) Mosh hardness: 9
E) Color: White

2: 95% High-alumina grinding ball
A) Al2O3 ≥ 95%  Sio2<3.8%, others:~3%
B) Water absorption <0.01%
C) Bulk density ≥ 3.7 g/cm3
D) Mosh hardness: 9
E) Color: White
F) self abrasion loss : <0.008%

3: 68% Medium alumina grinding ball series :
A) Al2O3 : 65%~75%
B) Bulk density ≥ 2.93g/cm3
C) Mosh hardness: 8 grade
D) self abrasion loss :0.01
E) Color : white or brown

92% Alumina grinding ball chemical and physical introduction :

Items	Proportion	Items	Proportion
Al2O3	92%	SiO2	<6.5%
others	~2%

 

Items	Proportion	Items	Proportion
Hardness: Mohr's	9	self Abrasion Loss (24hour)	<0.01%
Density(g/cm3)	3.6g/cm3	Water Absorption	<0.01%
Color	White	Ball method	By cool isostatic-pressing Or by rolling

95% Alumina ball chemical and physical introduction :

Items	Proportion	Items	Proportion
Al2O3	95%	SiO2	<3%
others	~2%

         

Items	Proportion	Items	Proportion
Hardness: Mohr's	9	self Abrasion Loss (24hour)	<0.01%
Density(g/cm3)	3.74g/cm3	Water Absorption	<0.01%
Color	White	Ball method	By cool isostatic-pressing Or by rolling

  68% Alumina ball chemical and physical introduction :

Items	Proportion	Items	Proportion
Al2O3	68.62%	SiO2	21.2%
others	~10.18%

  

Items	Proportion	Items	Proportion
Hardness: Mohr's	7-8	self Abrasion Loss (24hour)	<0.03%
Density(g/cm3)	3.g/cm3	Water Absorption	<0.1%
Color	creamy white	Ball method	By cool isostatic-pressing Or by rolling