Silicone for Clothing Logo Screen Printing Eco-Friendly Glossy Effect Silicone Ink Features

High Quality Silicone Ink For Label Making THS-1340T is a two-component addition-molded liquid silicone rubber. It has excellent weather resistance, good dimensional stability, moderate hardness, good fluidity, high transparency, non-toxic and environmentally friendly, and good adhesion to various textile fabrics. , Heat resistance up to 250 ºC or more, widely used in the production of clothing signs.


The main technical parameters:

projectvalue
Before curingExterior(Base rubber/Hardener)Translucent/Colorless viscous liquid
Viscosity(Base rubber/Hardener)/mPa.s70000/3000
Operating time(25ºC)/min90
After curingHardness/Shore A42
Density/g.cm-31.10
Tensile Strength/MPa5.0
Elongation/%260
Tear strength/kN.m-115
Linear shrinkage/%0.1
                                                                          (Non-specific value)
 

Clothing embossed silica gel  can be used for the production of clothing trademarks,but also for cloth pressing and pressing.It can be used as auxiliary material for clothing production,and can also be used as logo.

 

Attention:

    This product is a platinum catalyst.Water,impurities,organic tin catalysts such as condensation gums,acids,alkalis and other organic compounds containing sulfur,phosphorus and nitrogen may aggect the curing of the gums.Do not mix or contact these substances during use.

 

Use method:

1. Mixing: The rubber material and curing agent are mixed at a weight ratio of 10 : 1 (the amount of curing agent will increase the curing agent will slow down the curing speed). The mixing can be performed manually or by using a stirring device.
2. Defoaming: The mixed compound should be degassed under vacuum before making a label or printing a trademark on the fabric. Under vacuum, the rubber volume can increase 4-5 times. Therefore, the defoaming container should be 4-5 times larger than the rubber volume. After a few minutes, the rubber volume returns to normal. When no bubbles escape on the surface (about Ten minutes) is the end of defoaming, and it can be carried out in a vacuum dryer when using a small amount.
3. Molding: After defoaming, the glue can be dispensed or scraped. The glue can be injected into the mold and heated to form.














Certificate



 

 Packaging, storage and transportation and precautions
• The base rubber in this series is packed in 20kg / per iron can.
• This series of products should be stored in a dry, ventilated and cool place to prevent rain and sunlight.
• Avoid contact with condensation type silicone rubber curing agents during operation. Also likely to cause the compound to not solidify are amines, sulfur and phosphorus compounds, and some metal salts. Avoid moisture ingress during use.
• The storage period of this series of products is one year, and the fluidity can be restored under the action of shearing force (strong stirring). It is recommended that the rubber material be stirred in a container first, and then added with a curing agent and stirred evenly. It can still be used after passing the retest.

Lead Time :

Quantity(Kilograms)1 - 200>200
Est. Time(days)3To be negotiated




About us
    When I choose a product,I want to know the manufacturer of the product to verify that my product is of high quality.So I also prepared our information for you, so you can choose us with confidence.



 

Main product
    In addition to the main products, our materials can also be used as raw materials for many products, such as cables, cosmetic molds, mechanical supplies, waterproof supplies.   

   

    If you have other needs, you can contact me first to inquire whether our silicone can meet your needs.  demand


 

FAQ

 

Product Tag:
Related categories:
Scroll to Top