| Curing Agent | Triglycidyl Isocyanurate(TGIC) | |||||||
| Hydroxy alkyl amide(HAA) | ||||||||
| Type of Resins | Item No. | Ratio PE/Crosslinker | Acid Value (mgKOH/g) | Viscosity(p/200ºC) /mpa.s | Tg Value (°C) | Cure cycle ºC/min | Key Features | |
| TGIC Based Polyester Resins | A902 | 93/7 | 30~35 | 4000~5000 | ≥64 | 200*10 | High gloss ,Excellent flow, weathering resistance and mechanical properties | |
| A903 | 93/7 | 30~35 | 4500~5500 | ≥62 | 200*10 | Super weathering resistance, Excellent mechanical properties,good flow | ||
| A906 | 93/7 | 30~35 | 4000~5000 | ≥65 | 200*10 | High gloss ,Excellent flow, boiling water resistance, mechanical properties | ||
| A907 | 93/7 | 29~35 | 5000~6000 | ≥67 | 200*10 | Good weathering resistance and mechanical properties,,suitable for texture powder coating | ||
| A801 | 96/4 | 18~24 | 5500~6500 | ≥65 | 200*10 | For dry blend matte system as fast component,good storage stability | ||
| A802 | 93/7 | 30~36 | 3800~4800 | ≥65 | 200*10 | Excellent flow,suitable for High gloss and matt | ||
| A808 | 90/10 | 48~55 | 2800~3800 | ≥66 | 200*10 | For dry blend matte system as fast component,good storage stability | ||
| A301 | 96/4 | 18~24 | 5000~6000 | ≥65 | 200*10 | Low cost resin,for dry blend matte system as fast component,good storage stability | ||
| A303 | 93/7 | 30~36 | 3600~4600 | ≥64 | 200*10 | Low cost resin,good flow and mechanical properties | ||
| A307 | 93/7 | 30~35 | 4800~6000 | ≥65 | 200*10 | Low cost resin,suitable for texture powder coating | ||
| A308 | 90/10 | 50~56 | 2600~3600 | ≥65 | 200*10 | Low cost resin,for dry blend matte system as fast component,good storage stability | ||
| Primid(HAA) Based Polyester Resins | H602 | 95/5 | 20~25 | 4000~5000 | ≥64 | 180*15 | Low cost resin,good flow and mechanical properties | |
| H604 | 96.5/3.5 | 18~24 | 6000~7500 | ≥61 | 180*15 200*10 | Low cost resin,based on hydroxy alkyl amide (HAA) ,good flow ,good overbake resistance to yellowing | ||
| Product Name | Powder Coating Polyester Resin | ||||
| Product Model | A307 | ||||
| Product Discription | A307 is a special carboxyl terminated polyester resin for HAA and TGIC double curing powder coatings at 200 ºC. A307 resin is used for general industrial sand grain and orange grain paint. It has good weather resistance, excellent boiling performance and mechanical properties, and can significantly reduce the formulation cost when combined with HAA | ||||
| Product appearance | White particles | ||||
| Viscosity (200 ° C,mpa.s) | 4800~6000 | ||||
| Acid Value(mgKOH/g) | 30~35 | ||||
| Glass Transition Temperature | ≥65 |
| Components | Net Wight | ||||
| A307 | 558 | ||||
| TGIC | 42 | ||||
| Titanium Dioxide | 300 | ||||
| Barium Sulfate | 90 | ||||
| Swelling Figure | 5 | ||||
| Sand grain agent | 5 |
| Squeeze | |||||||
| Screw | 40HZ | ||||||
| Zone 1 temperature | 100 | ||||||
| Zone 2 temperature | 110 | ||||||
| Application | |||||||
| Film thickness, substrate | 60-80um film thickness, 0.5mm cold rolled steel plate | ||||||
| Gloss | ≥90% | ||||||
| Recoil(kg.cm) | 50 | ||||||
| Foreflush(kg.cm) | 50 | ||||||
| Adhesion(grade) | 0 | ||||||
| Foshan Faxus New Material Company Limited |
| Please be noticed that the information and testing results represent above is for reference only. Results and figures above will be changed based on different testing conditions. Customers are suggested to design and test the product formula based on the actual conditions of production properties. |