About PVC Compounds:
Cable PVC compounds are thermoplastic materials derived from processing polyvinylchloride compositions, produced as granules. Various properties are imparted to compounds depending on applications and item operation conditions. This is achieved by using plasticizers, stabilizers and modifiers in various combinations in compositions.
PVC based plasticizers have considerable mechanical strength and water resistance, high thermal resistance to low temperatures, good insulation properties , abrasion, acid and alkali resistant. PVC based compounds are readily welded and glued.
Cable PVC compounds are use in the cable and conductor industry for manufacture of insulation and protective wire and cable sheaths. The main final consumers of the PVC based cable and conductor products are energy and construction industries.
Technical Data Sheet:
| Technical Data Sheet | ||||
| Product specification | 70ºCsheath material Proportion1.40 | |||
| Property | Unit | Standard Range | Test Value | |
| 1 | Operating Temperature | ºC | 70 | 70 |
| 2 | Shore Hardness A | A | 83±4 | 83±4 |
| 3 | Specific Gravity | 1.40±0.02 | 1.40±0.02 | |
| 4 | Tensile Strength before ageing | Mpa | ≥15.0 | 17.2 |
| 5 | Elongation at break before ageing | % | ≥180 | 306 |
| 6 | Ageing conditions | 100±2ºC,168h | ||
| 7 | Retention of tensile strength after ageing | % | ±20 | 10 |
| 8 | Retention of elongation after ageing | % | ±20 | negative11 |
| 9 | Loss of mass | ≤23 | 11 | |
| 10 | Cold Shock Oon negative25ºC | 15/30 | 3/30 | |
| Remark | Hereinbefore tests and the using apparatus are in accordance with GN/T8815 | |||
1.Technical specifications of 70 ºC pvc compound
| Tensile strength | MPa | 20.5 |
| Fracture tensile strain | % | 320 |
| Ageing temperature | ºC | 100 |
| Ageing time | h | 168 |
| Tensile strength after ageing | MPa | 22.5 |
| Max change of tensile strength | % | +12 |
| After ageing fracture tensile strain | % | 290 |
| Max change of fracture tensile strain | % | -10 |
| Thermal deformation | % | 28 |
| Thermal ageing quality loss | g/m2 | 19 |
| 200ºC thermal stability time | min | 90 |
| 20ºC volume resistivity | Ω.cm | 2.0*1011 |
2. Technical specifications of 90 ºC pvc resin compound
| Tensile strength | MPa | 20 |
| Fracture tensile strain | % | 330 |
| Ageing temperature | ºC | 100 |
| Ageing time | h | 240 |
| Tensile strength after ageing | MPa | 21.5 |
| Max change of tensile strength | % | +8 |
| After ageing fracture tensile strain | % | 310 |
| Max change of fracture tensile strain | % | -6 |
| Thermal deformation | % | 28 |
| Thermal ageing quality loss | g/m2 | 9 |
| 200ºC thermal stability time | min | 120 |
| 20ºC volume resistivity | Ω.cm | 2.0*1010 |
About us:
Jiangxi Longtai New Material Co., Ltd, founded in 2002, was successfully listed the New OTC Market in 2016, stock code: 836898. Longtai is specialized in the development and sales of all kinds of new materials, wire&cable materials and ariculture products. It has passed ISO9001:2008. All product meet RoHS and REACH by SGS. More than 30% of products are exported to Europe, America, Janpan, Southeast Asia and Africa, and so on.
Main Products:
1. fibrillatedPP twine,PP rope,PP split film rope,PP packing rope,baler twine,banana rope,all kinds of agricultural rope,garden rope.
2.PP cable filler yarn,optical cable filler yarn,flame retardant filler yarn,Halogen FR PP filler,cable material.
3.Sewing thread,polyester thread,nylon thread,polyester twine.
4.Cotton yarn,cotton twine,and recycled cotton yarn.
5.Aramid yarn,polyester yarn,nylon yarn and other special fiber.
6.Cotton paper,AL-PET tape,glass fiber and other filling and shielding materials.
After-Sale Service:
1.Profession:We have Professional sales and Any of your inquiry will be treated within 8 hours in a exactly quotation.
2.Price:The best competitive price,we are factory that can control the lowest cost.
3.Service:We will follow your order from inquiry to shipment,ensure the goods be produced as per your requirement fully and highest quality.