Complaint
| Item | Unit | Test result | Test method |
| Appearance | --- | Light yellow liquid | GB/T8237 |
| Solid content | % | 72.0~77.0 | GB/T-7193-4.3 |
| Acid value | mgKOH/g | 19.0~29.0 | GB/T 2895 |
| Viscosity(mPa ·s) | mPa·s | 8000~10000 | JIS-K-6901-5.5.1 |
| Gel time (min) | min | 6.0~12.0 | JIS-K-6901-5.9 |
| Maximum exothermic temperature | ºC | >90 | JIS-K-6901-5.9 |
| Item | Unit | Test result | Test method |
| Tensile Strength | MPa | 70 | GB/T2567 |
| Tensile modulus | MPa | 3700 | |
| Elongation at break | --- | 2. 5% | |
| Flexural strength | MPa | 130 | |
| Flexural modulus | MPa | 3800 | |
| Impact strength | KJ/m2 | 12 | |
| Barcol hardness | --- | 48 | GB/T3854 |
| Heat distortion temperature | ºC | 76 | GB/T1634 |
Applied to cast and fiberglass, like excellent handicrafts, body of automobile, etc.