Polycarbonate (PC) Resin Containing 20% Carbon Fiber for Large Format Additive

Min.Order: 25

Product origin: Dongguan, Guangdong, China

Infringement complaint:

Complaint

US$ 0.27 ~ 2.42

Description

Polycarbonate (PC) resin containing 20% carbon fiber for Large Format Additive
https://forever-plastics.en.made-in-china.com/product-list-1.html

Product Description
LNP THERMOCOMP DC004XXAR1 compound is based on Polycarbonate (PC) resin containing 20% carbon fiber for Large Format Additive Manufacturing (LFAM) applications. Added features of this grade include: Higher Stiffness vs. glass fiber, Higher Strength, Higher Temperature Performance and Higher Throughput compared to ABS and PPE, as well as Excellent Ductility and Smooth Surface Finish.
General
Form	Resin Pellets
Filler			20 % Carbon Fiber
Feature			Good Thermal High Impact	Good Hardness
Uses		Industria
Physical		Nominal Value		Test Method
Density / Specific Gravity		1.27		ASTM D792
Mechanical		Nominal Value		Test Method
Tensile Stress				ASTM D638 Modified
XZ Orientation;5mm/min		124 MPa
ZX Orientation;5mm/min		48 MPa

Tensile Stiffness

ASTM D638
Modified

XZ Orientation;5mm/min;Tensile Stiffness (K) is structura1l.15E+4 MPa
property defined as the stress/strain in the linear region
of the stress-strain curve. Value depends on the
geometry/shape and boundary/surrounding conditions

ZX Orientation;5mm/min

3000 MPa

Flexural Stress XZ Orientation;5mm/min ZX Orientation;5mm/min	66 MPa 164 MPa		ASTM D790 Modified
Tensile Strain XZ Orientation;5mm/min ZX Orientation;5mm/min	1.6 % 2 %		ASTM D638 Modified
Thermal	Nominal Value		Test Method
Heat Deflection Temperature[HDT], Annealed(3.2 mm;1.82 MPa)	144 °C		ASTM D648
Processing		Nominal Value
Extruder L/D<Extrusion>		24
Drying Temperature<Extrusion>		120 °C
Drying Time<Extrusion>		4 hrs
Maximum Moisture Content<Extrusion>		0.02 %
Barrel - Zone 1 Temperature<Extrusion>		250 - 280 °C
Barrel - Zone 2 Temperature<Extrusion>		260 - 290 °C
Barrel - Zone 3 Temperature<Extrusion>		260 - 290 °C
Barrel - Zone 4 Temperature<Extrusion>		260 - 290 °C
Nozzle Temperature<Extrusion>		260 - 290 °C
Melt Temperature<Extrusion>		260 - 290 °C
Bed Temperature<Extrusion>		100 - 120 °C
Extruder Pressure<Extrusion>		< 11 MPa

Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.

Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.

With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry