Complaint
| General | ||
| Form Resin Pellets | ||
| Filler 30 % Glass Fiber | ||
| Physical | Nominal Value | Test Method |
| Density / Specific Gravity | 1.12 g/cm³ | ISO 1183 |
| Linear Mold Shrinkage | ||
| Flow;average process;150x80x2 mm | 0.2 % | |
| average process;150x80x2 mm;Acrosss flow | 1 % | |
| Melt Flow(2.16 kg;230 °C) | 2.0 g/10min | ISO 1133 |
| Ball Indentation Hardness | 124 MPa | ISO 2039 |
| Mechanical | Nominal Value | Test Method |
| Tensile Strength, Yield | 97.0 MPa | ISO 527-2 |
| Elongation at Break | 3.0 % | ISO 527-2 |
| Elongation at Yield | 2.8 % | ISO 527-2 |
| Tensile Modulus | 6800 MPa | ISO 527-2 |
| Flexural Strength | 130 MPa | ISO 178 |
| Flexural Modulus | 6200 MPa | ISO 178 |
| Izod Impact, Notched, ISO Temperature; -20 °C Temperature; 23 °C | 8.00 kJ/m² 11.0 kJ/m² | ISO 108-1A |
| C harpy Impact Unnotched Temperature; 23 °C Temperature; 23 °C | 45 kJ/m² 50 kJ/m² | ISO 179 1eU |
| C harpy Impact, Notched Temperature; -30 °C Temperature; -20 °C Temperature; 23 °C | 8 kJ/m² 9 kJ/m² 11 kJ/m² | ISO 179 1eA |
| Thermal | Nominal Value | Test Method |
| Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa | 159 °C 145 °C | ISO 75-2 |
| Vicat Softening Point 5.1 kg 1.02 kg | 135 °C 165 °C | ISO 306 |
| Processing | Nominal Value | |
| Processing Temperature | 230 - 280 °C | |
| Feed Temperature | 40.0 - 80.0 °C | |
| Mold Temperature | 30.0 - 50.0 °C | |
| Injection Velocity | 100 - 200 mm/sec | |
| Hold Pressure | 30.0 - 60.0 MPa |