| Celanex 3216 is a non-exuding (UL and CSA approved V-0 at 1/32 inch and 5V at 1/8 inch ),15% fiberglass reinforced poly butylene terephthalate which has an excellent balance of mechanical properties and processability. It is well suited for electrical connector applications where its UL approved 50% regrind use capability allows maximum use of purchased product. | ||||
| General | ||||
| Form | Resin Pellets | |||
| Filler | 15 % Glass Fiber | |||
| Feature | Non-Exuding | |||
| UL Yellow Card | E45575-239383 | |||
| Uses Connector | Electrical | |||
| Physical | Nominal Value | Test Method | ||
| Shore Hardness, Shore D(15 sec) | 82 | ISO 868 | ||
| Thermal | Nominal Value | Test Method | ||
| Heat Deflection Temperature, Unannealed | ||||
| 0.45 MPa | 217 °C | ISO 75-2/B | ||
| 1.8 MPa | 187 °C | ISO 75-2/A | ||
| 8 MPa | 95.0 °C | ISO 75-2/C | ||
| Glass Transition Temperature(10 °C;min) | 60.0 °C | ISO 11357-2 | ||
| Vicat Softening Temperature | 206 °C | ISO 306/B50 | ||
| Melting Point(10 °C/min) | 225 °C | ISO 11357-3 | ||
| CLTE, Flow | 3.6E-5 cm/cm/°C | ISO 11359-2 | ||
| CLTE, Transverse | 1.0E-4 cm/cm/°C | ISO 11359-2 | ||
| Flame Rating 0.38 mm 3 mm | V-0 5VA | UL 94 | ||
| Oxygen Index | 27 - 32 % | ISO 4589-2 | ||
| Electrical | Nominal Value | Test Method | ||
| Surface Resistivity | 1.0E+15 ohms | IEC 60093 | ||
| Volume Resistivity | 1.0e+15 ohms ·cm | IEC 60093 | ||
| Electric Strength | 30 kV/mm | IEC 60243-1 | ||
| Relative Permittivity 100 Hz 1.0e+6 Hz | 3.70 3.50 | IEC 60250 | ||
| Dissipation Factor 100 Hz 1.0e+6 Hz | 3.3E-3 0.016 | IEC 60250 | ||
| Comparative Tracking Index | 250 V | IEC 60112 | ||
| Processing | Nominal Value | |||
| Drying Temperature<Injection> | 120 - 130 °C | |||
| Drying Time<Injection> | 4.0 hr | |||
| Hopper Temperature<Injection> | 20 - 50 °C | |||
| Rear Temperature<Injection> | 230 - 240 °C | |||
| Middle Temperature<injection> | 235 - 250 °C | |||
| Front Temperature<Injection> | 235 - 250 °C | |||
| Nozzle Temperature<Injection> | 250 - 255 °C | |||
| Processing Temp, Melt<Injection> | 235 - 280 °C | |||
| Mold Temperature<Injection> | 65 - 93 °C | |||
| Injection Rate<Injection> | Moderate-Fast | |||
| Feeding zone<Injection> | 230 - 240 °C | |||
| Hot Runner Temperature<Injection> | 250 - 260 °C | |||
| Zone4 temperature<Injection> | 240 - 255 °C | |||