Complaint
| General | ||||
| Form | Resin Pellets | |||
| Filler | 16 % Glass Fiber | |||
| Feature | Good Thermal | High Mechanical Strength Good Hardness And Rigidity | ||
| Usage | Automotive Furniture Industrial Applications | |||
| Physical | Nominal Value | Test Method | ||
| Density / Specific Gravity | 1.16 g/cm³ | ISO 1183 | ||
| Melt Volume-Flow Rate, MVR(220 °C;10 kg) | 3.0 cm³/10 min | ISO 1133 | ||
| Molding Shrinkage | 0.20 - 0.40 % | ISO 294-4 | ||
| Ash Content | 16 % | |||
| Ball Indentation Hardness | 135 MPa | ISO 2039-1 | ||
| Mechanical | Nominal Value | Test Method | ||
| Tensile Modulus | 5500 MPa | ISO 527-2 | ||
| Tensile Stress, Yield(23 °C) | 74.0 MPa | ISO 527-2 | ||
| Tensile Stress, Break(23 °C) | 74.0 MPa | ISO 527-2 | ||
| Tensile Strain, Break(23 °C) | 2.0 % | ISO 527-2 | ||
| Flexural Modulus(23 °C) | 5400 MPa | ISO 178 | ||
| Flexural Stress(23 °C) | 101 MPa | ISO 178 | ||
| C harpy Notched Impact Strength -30 °C 23 °C | 5.0 kJ/m² 6.0 kJ/m² | ISO 179 1eA | ||
| C harpy Unnotched Impact Strength -30 °C 23 °C | 20 kJ/m² 18 kJ/m² | ISO 179 1eU | ||
| Notched Izod Impact Strength -30 °C 23 °C | 5.0 kJ/m² 7.0 kJ/m² | ISO 180/1A | ||
| Thermal | Nominal Value | Test Method |
| Heat Deflection Temperature, Annealed 0.45 MPa;4 h;80 °C 1.8 MPa;4 h;80 °C | 106 °C 102 °C | ISO 75-2/B ISO 75-2/A |
| Vicat Softening Temperature | 107 °C 105 °C | ISO 306/B120 ISO 306/B50 |
| CLTE, Flow | 4.0E-5 cm/cm/°C | ISO 11359-1 |
| Burning rate(2 mm) | 20 mm/min | ISO 3795 |
| Flame Rating(1.5 mm) | HB | IEC 60695-11-10 |
| Glow Wire Flammability Index(2 mm) | 700 °C | IEC 60695-2-12 |
| Electrical | Nominal Value | Test Method |
| Surface Resistivity | 1.0E+14 ohms | IEC 62631-3-1 |
| Volume Resistivity | > 1.0E+15 Ohms ·cm | IEC 62631-3-1 |
| Electric Strength(1 mm) | 32 kV/mm | IEC 60243-1 |
| Relative Permittivity 100 Hz 1.0e+6 Hz | 2.90 3.10 | IEC 62631-2-1 |
| Dissipation Factor 100 Hz 1.0e+6 Hz | 9.0E-3 6.0E-3 | IEC 62631-2-1 |
| Comparative Tracking Index | 575 V | IEC 60112 |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 80 °C | |
| Drying Time<Injection> | 2.0 - 4.0 hr | |
| Processing Temp, Melt<Injection> | 230 - 260 °C | |
| Mold Temperature<Injection> | 60 - 80 °C | |
| Injection Velocity<Injection> | 14 m/min |
| Product Description | ||||
| A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up. | ||||
| General | ||||
| Form | Resin | Pellets | ||
| Physical | Nominal Value | Test Method | ||
| Density / Specific Gravity | 1.40 g/cm³ | |||
| Water Absorption | 0.21 % | ASTM D570 | ||
| Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
| Linear Mold Shrinkage | 2.2 % | |||
| Linear Mold Shrinkage, Transverse | 1.8 % | |||
| Hardness, Rockwell R | 111 | ASTM D785 | ||
| Mechanical | Nominal Value | Test Method | ||
| Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
| Elongation at Break | 30 % | ASTM D638 | ||
| Flexural Strength | 52.0 MPa | ASTM D790 | ||
| Flexural Modulus | 2100 MPa | ASTM D790 | ||
| Compressive Strength | 66.0 MPa | ASTM D695 | ||
| Shear Strength | 40.0 MPa | ASTM D732 | ||
| Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C | 50 J/m 30 J/m | ASTM D256 | ||
| Thermal | Nominal Value | Test Method | ||
| Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa | 152 °C 106 °C | ASTM D648 | ||
| Flammability, UL94 | HB | UL 94 | ||