Complaint
| General | |||||
| Form | Resin Pellets | ||||
| Filler | Stainless Steel Fiber | ||||
Feature | Electrically Conductive Non-Chlorinated | Emi/Rfi Shielding | Non-Brominated & Non- Chlorinated Flame Retardant | ||
| Usage | Consumer Electrical | Packaging | Industria | ||
| Physical | Nominal Value | Test Method | |||
| Density / Specific Gravity | 1.46 g/cm³ 1.46 g/cm³ | ASTM D792 ISO 1183 | |||
| Moisture Absorption | |||||
| 23 °C;50% RH/24 hrs | 0.08 % | ASTM D570 | |||
| 50% RH;23 °C | 0.04 % | ISO 62 | |||
| Mechanical | Nominal Value | Test Method |
| Izod Impact, Unnotched | ||
| 23 °C | 350 J/m | ASTM D4812 |
| -30 °C | 330 J/m | ASTM D4812 |
| 80*10*4;23 °C | 21 kJ/m² | ISO 180/1U |
| 80*10*4;-30 °C | 21 kJ/m² | ISO 180/1U |
| Izod Impact, Notched | ||
| 23 °C | 60 J/m | ASTM D256 |
| -30 °C | 44 J/m | ASTM D256 |
| 80*10*4;23 °C | 6 kJ/m² | ISO 180/1A |
| 80*10*4;-30 °C | 5 kJ/m² | ISO 180/1A |
| Multiaxial Impact | 4 J | ISO 6603 |
| Instrumented Dart Impact, Total Energy(23 °C) | 11 J | ASTM D3763 |
| C harpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp =62 mm 0) | 7 kJ/m² | ISO 179 1eA |
| Tensile Stress, Break | ||
| 5 mm/min;Type I | 60 MPa | ASTM D638 |
| 5 mm/min | 62 MPa | ISO 527 |
| Tensile Strain, Break | ||
| 5 mm/min;Type I | 1.8 % | ASTM D638 |
| 5 mm/min | 1.8 % | ISO 527 |
| Tensile Modulus | ||
| 50 mm/min | 6000 MPa | ASTM D638 |
| 1 mm/min | 5800 MPa | ISO 527 |
| Flexural Stress, Yield | ||
| 1.3 mm/min;50 mm;span | 90 MPa | ASTM D790 |
| 2 mm/min | 105 MPa | ISO 178 |
| Flexural Stress, break(1.3 mm/min;50 mm;span) | 90 MPa | ASTM D790 |
| Flexural Modulus(1.3 mm/min;50 mm;span) | 5300 MPa | ASTM D790 |
| Flexural Strain, Break(2 mm/min) | 2.8 % | ISO 178 |
| Thermal | Nominal Value | Test Method |
| UL Recognized(1.5 mm) | V-0 | UL 94 |
| Vicat Softening Temperature | ||
| Rate A/50 | 101 °C | ASTM D1525 |
| Rate B/50 | 105 °C | ASTM D1525 |
| Rate A/50 | 102 °C | ISO 306 |
| Rate B/120 | 105 °C | ISO 306 |
| Heat Deflection Temperature[HDT], Unannealed 3.2 mm;1.82 MPa 1.82 MPa;6.4 mm | 94 °C 96 °C | ASTM D648 |
| CTE, Flow | ||
| -40 - 40 °C | 3.1E-05 1/°C | ASTM E831 |
| 23°C to 60°C | 2.9E-05 1/°C | ISO 11359-2 |
| CTE, XFlow | ||
| -40 - 40 °C | 5.8E-05 1/°C | ASTM E831 |
| 23°C to 60°C | 7.4E-05 1/°C | ISO 11359-2 |
| HDT/Af(1.8) | 96 °C | ISO 75/Af |
| Relative Temp Index, Elec | 60 °C | UL 746B |
| Relative Temp Index, Mechanical with Impact | 60 °C | UL 746B |
| Relative Temp Index, Mechanical without Impact | 60 °C | UL 746B |
| Electrical | Nominal Value | Test Method |
| Volume Resistivity | 1.0E+04 - 1.0E+06 ohms ·cm | ASTM D257 |
| Surface Resistivity | 1000 - 1.0E+06 ohms | ASTM D257 |
| Static Decay(5000V to <50V) | < 0.01 Seconds | FTMS101B |
| Processing | Nominal Value |
| Drying Temperature<Injection> | 85 - 90 °C |
| Drying Time<Injection> | 3 - 4 hrs |
| Maximum Moisture Content<Injection> | 0.04 % |
| Melt Temperature<Injection> | 270 - 300 °C |
| Nozzle Temperature<Injection> | 265 - 300 °C |
| Front, Zone 3 Temperature<Injection> | 265 - 300 °C |
| Middle, Zone 2 Temperature<Injection> | 260 - 300 °C |
| Rear, Zone 1 Temperature<Injection> | 260 - 300 °C |
| Mold Temperature<Injection> | 60 - 100 °C |
| Back Pressure<Injection> | 4 MPa |
| Screw Speed <Injection> | 30 - 100 rpm |