Product Description | |||
Features: low odor; low residue; low gloss Application: automotive interior parts; modified use; small appliances | |||
General | |||
Form | Resin Pellets | ||
Feature Low Odor Low Gloss Low Residuals | |||
Uses | Interior Automotive Components | White Goods & Small Appliances | |
Physical | Nominal Value | Test Method | |
Melt Volume Rate, MVR | ISO 1133 | ||
5 kg;200 ºC | 2.6 cm³/10 min | ||
220 ºC;10 kg | 25 cm³/10 min | ||
Hardness 116 | ASTM D785 | ||
Density / Specific Gravity(23 ºC) 1.04 g/cm³ | ISO 1183 | ||
Mechanical | Nominal Value | Test Method | |
Tensile Strength(50 mm/min) 41 MPa | ISO 527 | ||
Elongation at Break(50 mm/min) 25 % | ISO 527 | ||
Flexural Strength(2 mm/min) 70 MPa | ISO178 | ||
Flexural Modulus(2 mm/min) 2400 MPa | ISO178 | ||
Notched Izod Impact Strength(23 ºC;4 mm) 16 kJ/m² | ISO 180 | ||
Charpy impact strength(23 ºC;4 mm) 16 kJ/m² | ISO 179 | ||
Thermal | Nominal Value | Test Method | |
Vicat Softening Temperature(10 N;50 ºC/hr) 105 °C | ISO 306 | ||
Deflection Temperature Under Load, Annealed(1.8 MPa) 100 °C | ISO 75-2 | ||
Deflection Temperature Under Load, Unannealed(1.8 MPa) | 80 °C | ISO 75-2 | |
Flammability(1.5 mm) | HB | UL-94 |
Product Description | ||||
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
General | ||||
Form | Resin | Pellets | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.40 g/cm³ | |||
Water Absorption | 0.21 % | ASTM D570 | ||
Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
Linear Mold Shrinkage | 2.2 % | |||
Linear Mold Shrinkage, Transverse | 1.8 % | |||
Hardness, Rockwell R | 111 | ASTM D785 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
Elongation at Break | 30 % | ASTM D638 | ||
Flexural Strength | 52.0 MPa | ASTM D790 | ||
Flexural Modulus | 2100 MPa | ASTM D790 | ||
Compressive Strength | 66.0 MPa | ASTM D695 | ||
Shear Strength | 40.0 MPa | ASTM D732 | ||
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C | 50 J/m 30 J/m | ASTM D256 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa | 152 °C 106 °C | ASTM D648 | ||
Flammability, UL94 | HB | UL 94 |