Polycarbonate Polymers Light Diffusion for Lamp PC Fr V0 Granules

Min.Order: 25

Product origin: Dongguan, Guangdong, China

Infringement complaint:

Complaint

US$ 0.27 ~ 2.42

Description

high heat polycarbonate copolymer enabling high aesthetics range of opaque colors

https://forever-plastics.en.made-in-china.com/product-list-1.html

General
Form Resin Pellets
Filler 30 % Glass Fiber
Feature	High Impact Lds	Enhanced Ductility Circuit Solution Good Surface Appearance
Usage	Automotive Electrical	Consumer Laser Direct Structuring
Physical Nominal Value Test Method
Density / Specific Gravity 1.47 ASTM D792
Melt Flow Rate[MFR] ASTM D1238
280 °C;2.16 kgf 10 g/10min
280 °C;5 kgf 27 g/10min
300 °C;1.2 kgf 16 g/10min
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) 13 cm³/10 min ASTM D1238

Mechanical	Nominal Value	Test Method
C harpy Impact, Unnotched(23 °C)	50 kJ/m²	ISO 179/2C
Izod Impact, Unnotched
23 °C	700 J/m	ASTM D4812
80104;23 °C	40 kJ/m²	ISO 180/1U
Izod Impact, Notched
23 °C	150 J/m	ASTM D256
80104;23 °C	14 kJ/m²	ISO 180/1A
C harpy Impact, Notched(23 °C)	14 kJ/m²	ISO 179/2C
Tensile Stress, Break
5 mm/min;Type I	120 MPa	ASTM D638
50 mm/min	120 MPa	ISO 527
Tensile Strain, Break
5 mm/min;Type I	2.4 %	ASTM D638
50 mm/min	2.4 %	ISO 527
Tensile Modulus
5 mm/min	8760 MPa	ASTM D638
1 mm/min	8840 MPa	ISO 527
Flexural Stress
	170 MPa	ASTM D790
	180 MPa	ISO 178
Flexural Modulus
	8020 MPa	ASTM D790
	8450 MPa	ISO 178

Thermal	Nominal Value	Test Method
Heat Deflection Temperature[HDT] 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa	126 °C 122 °C	ASTM D648
CTE, Flow -40 - 40 °C -40 - 40 °C	2.1e-05 1/°C 2.1e-05 1/°C	ASTM E831 ISO 11359-2
CTE, XFlow -40 - 40 °C -40 - 40 °C	6.9e-05 1/°C 7.1e-05 1/°C	ASTM E831 ISO 11359-2
HDT/Bf(0.45)	127 °C	ISO 75/Bf
HDT/Af(1.8)	124 °C	ISO 75/Af
Processing		Nominal Value
Drying Temperature<Injection>		110 °C
Drying Time<Injection>		3 - 4 hrs
Melt Temperature<Injection>		270 - 295 °C
Nozzle Temperature<Injection>		270 - 295 °C
Front, Zone 3 Temperature<Injection>		270 - 295 °C
Middle, Zone 2 Temperature<Injection>		270 - 295 °C
Rear, Zone 1 Temperature<Injection>		270 - 295 °C
Mold Temperature<Injection>		100 - 120 °C

Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.

Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.

With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry

Forward

Related products