| General | ||||
| Form Resin Pellets | ||||
| Filler 15 % Stainless Steel Fiber | ||||
| Electrically Conductive | Emi/Rfi Shielding | High Impact | ||
| Feature | Non-Brominated & Non-Chlorinated Flame Retardant | Non-Chlorinated | ||
Uses | Consumer Electrical | Packaging | Industria | |
| Physical | Nominal Value | Test Method | ||
| Mold Shrinkage, Flow(24 hrs) | 0.4 - 0.7 % | ISO 294 | ||
| Mold Shrinkage, XFlow(24 hrs) | 0.5 % | ISO 294 | ||
| Density / Specific Gravity | 1.29 g/cm³ | ISO 1183 | ||
| Mechanical | Nominal Value | Test Method | ||
| Izod Impact, Unnotched | ||||
| 23 °C | 1790 J/m | ASTM D4812 | ||
| 80*10*4;23 °C | 85 kJ/m² | ISO 180/1U | ||
| Izod Impact, Notched | ||||
| 23 °C | 124 J/m | ASTM D256 | ||
| 80*10*4;23 °C | 14 kJ/m² | ISO 180/1A | ||
| Tensile Stress, Yield | 57 MPa | ISO 527 | ||
| Tensile Stress, Break | 55 MPa | ISO 527 | ||
| Tensile Strain, Yield | 3.8 % | ISO 527 | ||
| Tensile Strain, Break | 4 - 8 % | ISO 527 | ||
| Tensile Modulus(1 mm/min) | 2800 MPa | ISO 527 | ||
| Flexural Stress | 80 MPa | ISO 178 | ||
| Flexural Modulus | 2600 MPa | ISO 178 | ||
| Thermal | Nominal Value | Test Method |
| CTE, Flow(-40 - 40 °C) | 5.6E-05 1/°C | ISO 11359-2 |
| CTE, XFlow(-40 - 40 °C) | 6.7e-05 1/°C | ISO 11359-2 |
| HDT/Bf(0.45) | 136 °C | ISO 75/Bf |
| HDT/Af(1.8) | 125 °C | ISO 75/Af |
| Electrical | Nominal Value | Test Method |
| Volume Resistivity | 1.0E+04 ohms ·cm | ASTM D257 |
| Surface Resistivity | 100 - 1.0E+04 ohms | ASTM D257 |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 120 °C | |
| Drying Time<Injection> | 4 hrs | |
| Maximum Moisture Content<Injection> | 0.02 % | |
| Melt Temperature<Injection> | 305 - 325 °C | |
| Front, Zone 3 Temperature<Injection> | 320 - 330 °C | |
| Middle, Zone 2 Temperature<Injection> | 310 - 320 °C | |
| Rear, Zone 1 Temperature<Injection> | 295 - 305 °C | |
| Mold Temperature<Injection> | 95 - 120 °C | |
| Back Pressure<Injection> | 0.2 - 0.3 MPa | |
| Screw Speed <Injection> | 30 - 60 rpm |