Glass fibres High thermal conductivity product based on Polyamide 6 (PA6) Special filler https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html
| Product Description | ||
| High thermal conductivity product based on Polyamide 6 (PA6). Special filler. Glass fibres. | ||
| General | ||
| Form Resin Pellets | ||
| Filler Glass Fiber | ||
| Feature Thermally Conductive | ||
| Physical Nominal Value Test Method | ||
| Density / Specific Gravity 2.62 g/cm³ ISO 1183 | ||
| Molding Shrinkage, Across Flow(2 mm;60 MPa) 0.70 - 0.85 % ISO 294-4 | ||
| Molding Shrinkage, Flow(2 mm;60 MPa) 0.25 - 0.40 % ISO 294-4 | ||
| Mechanical Nominal Value Test Method | ||
| Tensile Modulus ISO 527-2/1 | ||
| 23 °C 12000 MPa | ||
| 60 °C 5800 MPa | ||
| 90 °C 4300 MPa | ||
| 120 °C 4100 MPa | ||
| 150 °C 2600 MPa | ||
| Tensile Stress, Break ISO 527-2/5 | ||
| 23 °C 80.0 MPa | ||
| 60 °C 55.0 MPa | ||
| 90 °C 40.0 MPa | ||
| 120 °C 30.0 MPa | ||
| 150 °C 20.0 MPa | ||
| Tensile Strain, Break ISO 527-2/5 | ||
| 23 °C 1.4 % | ||
| 60 °C 1.9 % | ||
| 90 °C 2.0 % | ||
| 120 °C 2.0 % | ||
| 150 °C 2.1 % | ||
| C harpy Notched Impact Strength(23 °C) 3.0 kJ/m² ISO 179 1eA | ||
| C harpy Unnotched Impact Strength(23 °C) 23 kJ/m² ISO 179 1eU | ||
| Thermal | Nominal Value | Test Method |
| Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa | 255 °C 225 °C | ISO 75-2/B ISO 75-2/A |
| Continuous Use Temperature(2.0e+4 hr) | 90.0 °C | ASTM E1641/E1877 |
| Vicat Softening Temperature | 245 °C | ISO 306/B50 |
| CLTE, Flow(30 - 100 °C) | 3.0E-5 cm/cm/°C | ISO 11359-2 |
| Thermal conductivity in plane(in plane) | 1.7 W/m-K | ASTM E1461 |
| Electrical | Nominal Value | Test Method |
| Surface Resistivity | 1.0E+12 ohms | ASTM D257 |