Product Description | |
Injection molding, Medium viscosity, High toughness at low temperature | |
General | |
Form Resin Pellets | |
Feature Low Temperature Impact F1 Medium Viscosity | |
Uses Telecommunications | |
Physical Nominal Value Test Method | |
Density / Specific Gravity(23 °C) 1.19 g/cm³ ISO 1183 | |
Melt Viscosity(300 °C;1.0e+3 s-1) 600 Pa. s ISO 11443-A | |
Melt Volume-Flow Rate, MVR(300 °C;1.2 kg) 10 cm³/10 min ISO 1133 | |
Molding shrinkage, parallel(60x60x2;500 bar) 0.72 % ISO 2577 | |
Molding shrinkage, normal(60x60x2;500 bar) 0.68 % ISO 2577 | |
Mechanical Nominal Value Test Method | |
Tensile Modulus(1 mm/min;23 °C) 2200 MPa ISO 527-1/-2 | |
Tensile Stress, Yield(5 mm/min;23 °C) 60.0 MPa ISO 527-1/-2 | |
Tensile Stress, Break(5 mm/min;23 °C) 70.0 MPa ISO 527-1/-2 | |
Tensile Strain, Yield(5 mm/min;23 °C) 5.5 % ISO 527-1/-2 | |
Tensile Strain, Break(5 mm/min;23 °C) 150 % ISO 527-1/-2 | |
Flexural Modulus(2 mm/min;23 °C) 2300 MPa ISO 178 | |
Flexural Stress(2 mm/min;23 °C) 90.0 MPa ISO 178 | |
Notched Izod Impact Strength ISO 7391 | |
23 °C;3 mm 70 kJ/m² | |
-20 °C;3 mm 60 kJ/m² | |
-30 °C;3 mm 60 kJ/m² | |
-40 °C;3 mm 60 kJ/m² | |
Thermal Nominal Value Test Method | |
Vicat Softening Temperature(120 °C/h;50 N) 136 °C ISO 306 | |
Flame Rating UL 94 | |
1.5 mm V-0 | |
2 mm 5VB | |
2.5 mm 5VB | |
Processing | Nominal Value |
Drying Temperature - Dry Air Dryer<Injection> | 100 °C |
Drying Time - Dry Air Dryer<Injection> | 4.0 hr |
Mold Temperature<Injection> | 80 °C |
Standard Melt Temperature<Injection> | 280 - 300 °C |