1.carbide copper alloy brazing rod it is made of by sintering tungsten carbide scrap and elastic matrix alloy,Outer layer of the special flux and coloring is marking scrap grade,the composition of sintering tungsten carbide scrap is mainly CO and WC,The hardness is HRA 89~91,tire body matal is Ni and copper alloy,strength can up to 690MPa, hardness HB≥160.
2.Common particle sizes :1/16" x 1/8" (1.6 x 3.2 mm) , 3/16" x 1/8" (3.2 x 4.8 mm) , 1/4" x 3/16" (4.8 x 6.4 mm) , 5/16" x 1/4" (6.4 x 7.9mm) , 3/8" x 5/16" (7.9 x 9.5 mm), 1/2" x 3/8" (9.5 x 12.7 mm).
3.length :280mm ,450mm
4. YG +CuSnZn or YG+CuSnZn+10% Ni
5.WC grit compositions : 70% ,60%,50%
| grade | particle sizes(mm) | Length of welding rod |
| YD-9.5 | 8.2~9.5 | 280 or 450mm |
| YD-8 | 6.4~8.2 | 280 or 450mm |
| YD-6.5 | 4.8~6.4 | 280 or 450mm |
| YD-5 | 3.2~4.8 | 280 or 450mm |
| YD-3 | 1.6~3.2 | 280 or 450mm |
| YD-10mesh | 10~18mesh | 280 or 450mm |
| YD-18mesh | 18~30mesh | 280 or 450mm |
| YD-30mesh | 30~50mesh | 280 or 450mm |
Usages:
it is mainly used for surfacing welding the oil, mining, coal mining, geology, construction and other industries in some serious wear and tear or artifacts of both cutting.Such as: milling shoes, grinding, centralizer, reamer, drill pipe joints, hydraulic cutter, scraper, plough planer knives, core bit, piling drill, twist drill, etc.
The oxyacetylene butt, the operating process is as follows:
(1) clean up the workpiece, make the welding workpieces surface with metallic luster.
(2) the flat position of welding, therefore can use the appropriate clamping fixture for control of surfacing layer thickness, thick piece of available.
(3) with a neutral flame preheating, flame core not contact surface, the distance to 25 mm is advisable.
(4) carbide surfacing welding layer.With YD type electrode surfacing, the use of neutral flame (can be slightly carbonizing flame) tip is steady on the workpiece surface movement, the flame of the alloy electrode heating (be careful not to make flame cone tip contact alloy particles), tire body in the electrode alloy melt, carbide particles are also falling.Before the tire body of molten metal solidification, the particles arrange, can use left hand of the alloy electrode fingers, or another person holding a base electrode or pull rod on graphite rod in a quick stir particles, making them evenly aligned neatly.Surfacing layer thickness control according to the requirements of design.
(5) after the workpiece welding, where no ventilation, slow cooling, cannot quench, conditional usable asbestos blanket cover.
(6) the workpiece after cooling to room temperature, if necessary, grinding surface surfacing to required size and shape.
(7) clean up the workpiece, remove all splash, slag, etc.
our factory specializes in manufacturing a series of Tungsten Carbide products.such as:
tungsten carbide Saw Tips
tungsten carbide Buttons for Rock Bits
tungsten carbide Inserts for Road Milling, Plaing Bits
tungsten Carbide Inserts for Coal Cutter Picks
tungsten Carbide Inserts for Snopw Plow Blades
tungsten Carbide Inserts for Mining Tools
tungsten Carbide finished or blank Round Rods (dia from 1.0 to 25.4 mm,length 1.0 to 330mm)
tungsten Carbide Tubes
tunsgten Carbide Rings
tungsten Carbide strips and plates
tunsgten Carbide tips for Debarking Bits
tungsten Carbide Brazed Inserts or Tips
tunsgten Carbide pins
Tire studs
tunsgten Carbide Blanks
tunsgten Carbide Wear-Parts
tungsten carbide circular cutter
alloy welding material,etc.