Complaint
| Product Description | |||||
| Description Halogen Free Flame Retardant, Heat Resistant Chemical Resistance, High Impact Application IT/OA Housing and Components (Adaptor) | |||||
| General | |||||
| Form | Resin Pellets | ||||
Feature | Non-Brominated & Non- Chlorinated Flame Retardant | Chemical Resistant High Impact | Good Thermal | ||
| UL Yellow Card | E248280-101511247 | ||||
| Uses | Housing | ||||
| Physical Nominal Value | Test Method | ||||
| Density / Specific Gravity 1.20 g/cm³ | ASTM D792 | ||||
| Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) 13 g/10min | ASTM D1238 | ||||
| Molding Shrinkage - Flow, Injection Molded(23 °C;3.2 mm) | 0.50 - 0.80 % | ASTM D955 | |||
| Mechanical Nominal Value | Test Method | ||||
| Tensile Strength, Yield, Injection molded(50 mm/min;23 61.8 MPa °C;3.2 mm) | ASTM D638 | ||||
| Tensile Elongation, Break, Injection Molded(50 mm/min;23 °C;3.2 mm) | 100 % | ASTM D638 | |||
| Flexural Modulus, Injection Molded(10 mm/min;23 °C;3.22160 MPa mm) | ASTM D790 | ||||
| Flexural Strength, Injection Molded(10 mm/min;23 °C;3.296.1 MPa mm) | ASTM D790 | ||||
| Notched Izod Impact, Injection Molded -30 °C;3.2 mm 23 °C;3.2 mm | 120 J/m 740 J/m | ASTM D256 | |||
| Thermal | Nominal Value | Test Method | |||
| Deflection Temperature Under Load, Unannealed, Injection Molded(1.8 MPa;6.4 mm) | 123 °C | ASTM D648 | |||
| Vicat Softening Temperature(120 °C/h;50 N;Rate B;Loading 2) | 135 °C | ASTM D1525 | |||
| RTI Elec | 80.0 °C | UL 746 | |||
| RTI Imp | 80.0 °C | UL 746 | |||
| RTI Str | 80.0 °C | UL 746 | |||
| Flame Rating 1.5 mm 2 mm | V-0 V-0 - 5VB | UL 94 | |||
| Processing | Nominal Value | ||||
| Drying Temperature<Injection> | 90 - 100 °C | ||||
| Drying Time<Injection> | 3.0 - 4.0 hr | ||||
| Suggested Max Moisture<Injection> | 0.020 % | ||||
| Rear Temperature<Injection> | 270 - 285 °C | ||||
| Middle Temperature<injection> | 275 - 290 °C | ||||
| Front Temperature<Injection> | 275 - 290 °C | ||||
| Nozzle Temperature<Injection> | 270 - 285 °C | ||||
| Processing Temp, Melt<Injection> | 275 - 290 °C | ||||
| Mold Temperature<Injection> | 80 - 100 °C | ||||
| Back Pressure<Injection> | 1.96 MPa | ||||
| Screw Speed <Injection> | 40 - 80 rpm | ||||