High performance cross-linked shrink film has demonstrated comparable or even better performance versus than
other POF shrink film. It is proved by versatility across a broad range of shrink equipment, especially high-speed
application. all-purpose shrink film with superior strength, strong seals, high abuse resistance and uperior optics and clarity.
ASTM Test Method | Typical Values | ||||
Gauge | 50 | 60 | 75 | 100 | |
Minimum Use Temperature | -50°C | -50°C | -50°C | -50°C | |
Maximum Storage Temperaturre (2-yr max.) | 32°C | 32°C | 32°C | 32°C | |
Shrink Air Temperature (°C) | 121°C-176°c | 121°C-176°c | 121°C-176°c | 121°C-176°c | |
Density @23 °c (g/cc) | D1505 | 0.925 | 0.925 | 0.925 | 0.925 |
Haze % | D1003 | 2.5 | 2.5 | 2.8 | 3.0 |
Gloss % | D2457 | 88 | 89 | 90 | 90 |
Instrumented Impact Strength (lbs) | D3763 | 14 | 19 | 23 | 33 |
Coefficient of Friction (film-to-film, kinetic) | D1894 | 0.3 | 0.3 | 0.3 | 0.3 |
Water Vapor Transmission Rate | F1249 | 2.0 | 1.5 | 1.2 | 0.9 |
Oxygen Transmission Rate | D3985 | 9000 | 8500 | 7500 | 5900 |
LD/TD | LD/TD | LD/TD | LD/TD | ||
Tensile Strength (psi) | D882 | 18000/19000 | 18000/19000 | 18000/19000 | 18000/19000 |
Elongation at Break (%) | D882 | 90/120 | 90/130 | 90/140 | 120/130 |
Modulus of Elasticity (psi @ 22 °c) | D882 (A) | 70000/71000 | 70000/71000 | 70000/71000 | 70000/71000 |
Tear Propagatioin (gms) | D1938 | 3.5/3.5 | 4.0/5.2 | 5.3/6.9 | 6.2/9.4 |
Free Shrink (%) | D2732 | ||||
@95 | 11/18 | 11/18 | 11/18 | 11/18 | |
@105 | 23/33 | 23/33 | 23/33 | 23/33 | |
@115 | 55/57 | 55/57 | 55/57 | 55/57 | |
@125 | 79/77 | 79/77 | 79/77 | 79/77 | |
@135 | 80/78 | 80/78 | 80/78 | 80/78 |