Item | Results |
Appearance | Color adjustable |
Viscosity (cps )@20ºC | 250 |
Solid content (%) | ≥65 |
surface dry time (h) | 2-4 |
Pot life (h) | 1 |
theoretical coverage | 0.13kg/m2(thickness 100um) |
Item | Test standard | Results |
pencil hardness | GB/T 6739-2006 | 2H |
bending test (cylindrical mandrel) mm | GB/T 6742-1986 | 1 |
breakdown resistance strength (kv/mm) | HG/T 3330-1980 | 250 |
impact resistance (kg·cm) | GB/T 1732 | 60 |
resistance to temperature changes (-40--150ºC) 24h | GB/9278-1988 | Normal |
adhesive strength (Mpa), metal base | ASTM D-3359 | 5A (highest) |
density g/cm3 | GB/T 6750-2007 | 1.03 |
Acid resistance 50% H2SO4 or15%HCl, 30d | No rust, no bubbles, no peel off |
Alkali resistance 50%NaOH, 30d | No rust, no bubbles, no peel off |
Salt resistance, 50g/L,30d | No rust, no bubbles, no peel off |
Salt spray resistance, 2000h | No rust, no bubbles, no peel off |
Oil resistance 0# diesel, 30d | No bubbles, no peel off |
( For reference: pay attention to the influence of ventilation, splash and spillage. Independent immersion testing is recommended if requires other specific data.) |
Substrate temperature | Surface dry time | Foot traffic | Solid dry |
+10ºC | 6h | 24h | 7d |
+20ºC | 3h | 12h | 6d |
+30ºC | 2h | 8h | 5d |