| Item | A component | B component |
| Appearance | light yellow liquid | Color adjustable |
| Specific gravity(g/m³) | 1.04 | 1.50 |
| Viscosity (cps)@25ºC | 40-60 | 100-200 |
| Solid content (%) | 75 | 90 |
| Mix ratio (by weight) | 1 | 1 |
| Surface dry time (h) | 1 | |
| Pot life (h)@25ºC | 1 | |
| Theoretical coverage (DFT) | 0.15kg/m2 film thickness 100μm | |
| Item | Test standard | Results |
| Pencil hardness | H | |
| Adhesive strength(Mpa)metal base | HG/T 3831-2006 | 9.3 |
| Adhesive strength(Mpa)concrete base | HG/T 3831-2006 | 2.8 |
| Impermeability | 2.1Mpa | |
| Bending test (cylindrical shaft) | ≤1mm | |
| Abrasion resistance (750g/500r) mg | HG/T 3831-2006 | 5 |
| Impact resistance kg·cm | GB/T 1732 | 50 |
| Anti-aging, accelerated aging 1000h | GB/T14522-1993 | Loss of light<1, chalking <1 |
| Acid resistance 40%H2SO4 or 10%HCI, 240h | no rust, no bubbles, no peel off |
| Alkali resistance 40%NaOH, 240h | no rust, no bubbles, no peel off |
| Salt resistance 60g/L, 240h | no rust, no bubbles, no peel off |
| Salt spray resistance 1000h | no rust, no bubbles, no peel off |
| Oil resistance, engine oil 240h | no rust, no bubbles, no peel off |
| Water resistance, 48h | No bubbles, no wrinkled, no color-changing, no peel off |
| (Note: The above chemical resistant property is obtained according to the GB/T9274-1988 test method, for reference only. Pay attention to the influence of ventilation, splash and spillage. Independent immersion testing is recommended if requires other specific data.) | |
| environment temperature | -5~+35ºC |
| humidity | ≤85% |
| dew point | ≥3ºC |
| Substrate temperature | Surface dry time | Foot traffic | Solid dry time |
| +10ºC | 2h | 24h | 7d |
| +20ºC | 1.5h | 8h | 7d |
| +30ºC | 1h | 6h | 7d |