Hexagon Head Railway Track Sleeper Screw Spike

What is screw spike?
Railroad spike, also know as rail spike. Railroad spikes. They are designed to maintain gauge between the running rails, securing the steel rail to the railroad tie. Rail spikes have various shapes serving for different functions. The materials for railroad spikes production can be carbon or stainless steel based on the requirement, and the surface of the spikes can be plain, black, hot dipped galvanized, or sherardized, etc. Among the various railroad spikes, dog spikes and the screw spikes are the most common types.

Screw spikes - a kind of railroad spike Railway screw spikes are usually used to fasten railway ties or sleepers and also they also can be used in conjunction with plastic ferrules, casted into concrete ties /sleepers. Rail screw spikes can be various in thread profiles, lengths, diameters and drive heads based on specific geographic requirements.

Types of rail screw spike

Product Name		Specification	Material	Surface	Standard
Screw Spike	Square Head,Hexagon Screw Spike	M22*145	S235JR,Q235, 45#, 55#, 35Cr,ect	Black Oil Zinc Paint Dacromet	UIC, ASTM, AREMA, DIN, GB, etc
		M22*155
		M22*165
		M22*185
		M22*195
		Other Size
	Conventional Spike	Square 16*165
		Shank Spike

Types of rail sleeper spike

Product Name	Type	Specification	Weight/KG	Surface	Standard
Sleeper Screw	Ss 1/130	M22*130	0.451	Black Oil Zinc Paint Dacromet	UIC, ASTM, AREMA, DIN, GB, etc
	Ss 1/150	M22*150	0.478
	Ss 2/180	M22*180	0.595
	Ss 5/150	M24*150	0.545
	Ss 6/150	M26*150	0.702
	Ss 7/180	M24*180	0.636
	Ss 8/140	M24*140	0.528
	Ss 8/150	M24*150	0.548
	Ss 24/165	M24*165	0.59

Grade of rail screw spike

Grade	4.6	5 .6	8.8	10.9
Material	Q235	35#	45#	40Cr
Mechanical	Tensile strength: ≥ 400Mpa	Tensile strength: ≥ 500Mpa	Tensile strength: ≥ 800Mpa	Tensile strength: ≥ 1000Mpa
	Yield strength: ≥ 240Mpa	Yield strength: ≥ 300Mpa	Yield strength: ≥ 640Mpa	Yield strength: ≥ 900Mpa
	Elongation: ≥ 22%	Elongation: ≥ 20%	Elongation: ≥ 12%	Elongation: ≥ 9%
	Cold bending: 90 degree	Cold bending: 90 degree	Cold bending: 90 degree	Cold bending: 90 degree
	without crack	without crack	without crack	without crack
Surface	plain (oiled) , Oxide black, Zinc, HDG, wax, bitumen, Dacromet, Sherardizing