Complaint
General PC with iced-clear color excellent electrical performance, meet UL standard
https://forever-plastics.en.made-in-china.com/product-list-1.html
| Product Description | ||||||
| General PC with iced-clear color and good mold release property for injection molding or extrusion. Application: decorative lamp shade, safety lens, contact lens case, thin electrical appliance, electronic parts, mechanical parts, lighting appliance Characteristic :high impact strength, high transparency, wide range of temperature application, excellent dimensional precision and stability, excellent electrical performance, meet UL standards IR grade is listed in NSF/ANSI standard 51 Food Equipment Materials. | ||||||
| General | ||||||
| Form Resin Pellets | ||||||
| Feature | Good Dimensional Good Transparency | High Impact Nsf | ||||
| Uses | Safety Glasses | Box Overwrap Flexible P k i | Electron & electric parts | |||
| ac ag ng | ||||||
| Physical Nominal Value Test Method | ||||||
| Density / Specific Gravity 1.20 g/cm³ ISO 1183 | ||||||
| Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) 7.0 g/10min ISO 1133 | ||||||
| Molding Shrinkage, Flow 0.50 - 0.70 % ASTM D955 | ||||||
| Water Absorption, Equilibrium(50% RH;23 °C) 0.23 % ISO 62 | ||||||
| Outdoor Suitability f2 UL 746C | ||||||
| Rockwell Hardness, M-Scale 50 ISO 2039-2 | ||||||
| Rockwell Hardness, R-Scale 120 ISO 2039-2 | ||||||
| Mechanical Nominal Value Test Method | ||||||
| Tensile Stress, Yield 65.0 MPa ISO 527-2 | ||||||
| Tensile Strain, Break 90 % ISO 527-2 | ||||||
| Flexural Modulus 2200 MPa ISO 178 | ||||||
| Flexural Stress 90.0 MPa ISO 178 | ||||||
| C harpy Notched Impact Strength 80 kJ/m² ISO 179 | ||||||
| Thermal | Nominal Value | Test Method | ||||
| Heat Deflection Temperature, Unannealed(1.8 MPa) | 125 °C | ISO 75-2/A | ||||
| CLTE, Flow | 6.5E-5 cm/cm/°C | ISO 11359-2 | ||||
| RTI Elec | 130 °C | UL 746 | ||||
| RTI Imp | 125 °C | UL 746 | ||||
| RTI Str | 130 °C | UL 746 | ||||
| Flame Rating 3 - 6 mm 0.4 - 2.9 mm | HB V-2 | UL 94 | ||||
| Electrical | Nominal Value | Test Method | ||||
| Volume Resistivity | > 1.0E+16 ohms ·cm | ASTM D257 | ||||
| Electric Strength | 30 kV/mm | IEC 60243-1 | ||||
| Dielectric Constant(1.0e+6 Hz) | 2.85 | IEC 60250 | ||||
| Dissipation Factor(1.0e+6 Hz) | 9.2E-3 | IEC 60250 | ||||
| Comparative Tracking Index, CTI | PLC 2 | UL 746 | ||||
| Optical | Nominal Value | Test Method | ||||
| Transmittance | 85.0 - 90.0 % | ISO 13468-1 | ||||
| Processing | Nominal Value | |||||
| Drying Temperature<Injection> | 120 °C | |||||
| Drying Time<Injection> | 5.0 - 8.0 hr | |||||
| Mold Temperature<Injection> | 80 - 120 °C | |||||
Forever Co.,Ltd