Polypropylene resin granules with 40% glass fiber reinforcement, chemically coupled, and impact modified. Melt flow rate can be adjusted for different applications. Various colors available. Specify "U" for UV stabilized and "H" for heat stabilized options.
General | ||
Form Resin Pellets | ||
Filler 40 % Glass Fiber | ||
Feature High Impact | Chemically Coupled | |
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.24 g/cm³ | ASTM D792 |
Molding Shrinkage, Flow(3.18 mm) | 0.30 % | |
Mechanical | Nominal Value | Test Method |
Tensile Strength, Yield | 86.2 MPa | ASTM D638 |
Tensile Elongation, Break | 3.0 % | ASTM D638 |
Flexural Modulus | 6210 MPa | ASTM D790 |
Flexural Strength | 121 MPa | ASTM D790 |
Notched Izod Impact(3.18 mm) | 120 J/m | ASTM D256 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed(1.8 MPa) | 138 °C | ASTM D648 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 °C | |
Drying Time<Injection> | 2.0 - 3.0 hr | |
Processing Temp, Melt<Injection> | 220 - 260 °C | |
Mold Temperature<Injection> | 30 - 60 °C |