Heat-Conducting Nylon PA6 Thermally Conductive Electrically Insulative Flame Retardant
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| Product Description |
| Thermally Conductive - Electrically Insulative - Flame Retardant |
| General |
| Form Resin Pellets |
| Feature Thermally Conductive Rohs |
| Physical Nominal Value Test Method |
| Density / Specific Gravity 2.11 g/cm³ |
| Mechanical Nominal Value Test Method |
| Tensile Modulus 8960.0 MPa ISO 527-1/2 |
| Tensile Strength 75.8 MPa ASTM D638 |
| Tensile Elongation, Yield 1.0 - 2.0 % ASTM D638 |
| Flexural Modulus 8270.0 MPa ASTM D790 |
| Flexural Strength 121.0 MPa ASTM D790 |
| Notched Izod Impact(Thickness; 3.2 mm) 37.0 J/m ASTM D256 |
| Unnotched Izod Impact(Thickness; 3.2 mm) 270.0 J/m ISO 180/1eU |
| Thermal Nominal Value Test Method |
| Flame Rating(Thickness; 1.5 mm) V-0 |
| Thermal conductivity through plane(through-plane) 0.7 W/m-K ASTM E1530 |
| Thermal conductivity in plane(in-plane) 1.3 W/m-K ASTM E1461 |
| Electrical Nominal Value Test Method |
| Surface Resistivity > 1.0E+14 ohms ASTM D257 |
| Processing Nominal Value |
| Drying Temperature 79.0 °C |
| Drying Time 4.0 hr |
| Dew Point -18.0 °C |
| Melt Temperature 282 - 304 °C |
| Mold Temperature 79 - 121 °C |
| Injection Pressure 68.9 - 124 MPa |
| Moisture Content 0.2 % |