Nylon 6 resin containing mineral and glass fiber for Non-Chlorinated Flame Retardant
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| Product Description | ||||||
| compound is based on Nylon 6 resin containing mineral and glass fiber. Added features of this grade include: Thermally Conductive, Electrically Insulative and Non-Brominated, Non-Chlorinated Flame Retardant. | ||||||
| General | ||||||
| Form | Resin Pellets | |||||
| Filler | ||||||
Feature | Thermally Conductive | Non-Brominated & Non- | Non-Chlorinated Electrically Isolative | |||
| Chlorinated Flame R t d t | ||||||
| UL Yellow Card | E207780 - 101282911 | |||||
Uses | Consumer Industria Building and Construction | Electrical | ||||
| Physical | Nominal Value | Test Method | ||||
| Density / Specific Gravity | 1.79 g/cm³ | ASTM D792 | ||||
| Mold Shrinkage, Flow(24 hrs) | 0.42 % | ASTM D955 | ||||
| Mold Shrinkage, XFlow(24 hrs) | 0.58 % | ASTM D955 | ||||
| Water Absorption | ||||||
| 24 hrs;23 °C | 0.04 % | ISO 62-1 | ||||
| 24 hrs;23 °C | 0.23 % | Method | ||||
| Moisture Absorption(50% RH;23 °C) | 0.04 % | ISO 62 | ||||
| UV light, water exposure/immersion | f2 | UL 746C | ||||
| Mechanical | Nominal Value | Test Method | ||||
| Izod Impact, Unnotched | ||||||
| 23 °C | 326 J/m | ASTM D4812 | ||||
| 80*10*4;23 °C | 23 kJ/m² | ISO 180/1U | ||||
| Izod Impact, Notched | ||||||
| 23 °C | 30 J/m | ASTM D256 | ||||
| 80*10*4;23 °C | 3 kJ/m² | ISO 180/1A | ||||
| Tensile Stress, Break | ||||||
| 5 mm/min;Type I | 98 MPa | ASTM D638 | ||||
| 5 mm/min | 108 MPa | ISO 527 | ||||
| Tensile Strain, Break | ||||||
| 5 mm/min;Type I | 1.3 % | ASTM D638 | ||||
| 5 mm/min | 1.3 % | ISO 527 | ||||
| Tensile Modulus | ||||||
| 5 mm/min | 1.3E+04 MPa | ASTM D638 | ||||
| 1 mm/min | 1.3E+04 MPa | ISO 527 | ||||
| Flexural Stress, Yield(1.3 mm/min;50 mm;span) | 167 MPa | ASTM D790 | ||||
| Flexural Stress, break | ||||||
| 1.3 mm/min;50 mm;span | 176 MPa | ASTM D790 | ||||
| 2 mm/min | 186 MPa | ISO 178 | ||||
| Flexural Modulus | ||||||
| 1.3 mm/min;50 mm;span | 1.2E+04 MPa | ASTM D790 | ||||
| 2 mm/min | 1.3E+04 MPa | ISO 178 | ||||
| Impact Strength | 2.4 - 27 kJ/m² | ISO R179 | ||||
| Thermal | Nominal Value | Test Method | ||||
| UL Recognized(≥ 0.8 mm) | V-0 | UL 94 | ||||
| Glow Wire Ignition Temperature [GWIT] 1 mm 3 mm | 750 °C 800 °C | IEC 60695-2-13 | ||||
| Glow Wire Flammability Index 3 mm 1 mm | 960 °C 960 °C | IEC 60695-2-12 | ||||
| Heat Deflection Temperature[HDT](0.45 MPa;3.2 mm) | 227 °C | ASTM D648 | ||||
| Heat Deflection Temperature[HDT], Unannealed(1.82 MPa;6.4 mm) | 215 °C | ASTM D648 | ||||
| CTE, Flow(40°C to 120°C) | 4.1E-05 1/°C | ASTM E831 | ||||
| CTE, XFlow(40°C to 120°C) | 8.5E-05 1/°C | ASTM E831 | ||||
| Thermal conductivity through plane | ||||||
| 10*10*3mm sample | 1.4 W/m-K | ASTM E1461-07 | ||||
| ?80*3mm discs | 0.9 W/m-K | ISO 22007-2 | ||||
| Thermal conductivity in plane | ||||||
| 25*0.4mm disc | 1.8 W/m-K | ASTM E1461-07 | ||||
| ?80*3mm discs | 1.9 W/m-K | ISO 22007-2 | ||||
| Ball Pressure Test(125°C +/- 2°C) | PASSES | IEC 60695-10-2 | ||||
| HDT/Bf(0.45) | 228 °C | ISO 75/Bf | ||||
| HDT/Af(1.8) | 208 °C | ISO 75/Af | ||||
| Relative Temp Index, Elec | 130 °C | UL 746B | ||||
| Relative Temp Index, Mechanical with Impact | 105 °C | UL 746B | ||||
| Relative Temp Index, Mechanical without Impact | 140 °C | UL 746B | ||||
| Electrical | Nominal Value | Test Method | ||||
| Surface Resistivity | > 1.E+15 ohms | ASTM D257 | ||||
| Dielectric Strength, in Oil(1 mm) | > 10 kV/mm | ASTM D149 | ||||
| Dielectric Constant, Dk(1.1e+9 Hz) | 4.84 | ASTM ES 7-83 | ||||
| Dissipation Factor, Df(1.1e+9 Hz) | 9.9E-03 | ASTM ES 7-83 | ||||
| Comparative Tracking Index | 600 V | IEC 60112 | ||||
| Comparative Tracking Index, CTI | PLC 0 | UL 746A | ||||
| Hot-wire Ignition, HWI ≥ 3 mm ≥ 1 mm ≥ 0.8 mm | PLC 0 PLC 2 PLC 3 | UL 746A | ||||
| High Amp Arc Ignition, HAI( ≥ 0.8 mm) | PLC 0 | UL 746A | ||||
| Processing | Nominal Value | |||||
| Drying Temperature<Injection> | 80 °C | |||||
| Drying Time<Injection> | 4 hrs | |||||
| Maximum Moisture Content<Injection> | 0.15 - 0.25 % | |||||
| Melt Temperature<Injection> | 270 - 295 °C | |||||
| Front, Zone 3 Temperature<Injection> | 270 - 290 °C | |||||
| Middle, Zone 2 Temperature<Injection> | 270 - 290 °C | |||||
| Rear, Zone 1 Temperature<Injection> | 260 - 275 °C | |||||
| Mold Temperature<Injection> | 85 - 100 °C | |||||
| Back Pressure<Injection> | 0.2 - 0.3 MPa | |||||
| Screw Speed <Injection> | 20 - 60 rpm | |||||