| Item | Unit | Technology Standard | ||||||
| Transmission Performance | ||||||||
| Attenuation at 1310nm | dB/km | ≤0.34 | ||||||
| Attenuation at 1550nm | dB/km | ≤0.20 | ||||||
| Attenuation at 1383nm | dB/km | ≤0.30 | ||||||
| Attenuation at 1625nm | dB/km | ≤0.24 | ||||||
| Attenuation discontinuity | dB | ≤0.03 | ||||||
| Attenuation-wavelength characteristic | dB/km | ≤0.03 | ||||||
| Zero dispersion wavelength | nm | 1300~1324 | ||||||
| Zero dispersion slope | ps/(nm2.km) | ≤0.092 | ||||||
| Dispersion at 1288-1339nm | ps/(nm.km) | ≤3.5 | ||||||
| Dispersion at 1271-1360nm | ps/(nm.km) | ≤5.3 | ||||||
| Dispersion at 1550nm | ps/(nm.km) | ≤18 | ||||||
| PMD | ps/ km | ≤0.2 | ||||||
| Cut-off Wavelength(λcc) | nm | ≤1260 | ||||||
| Macro-bend loss (1550nm) | dB | 30mm radius100turns, ≤0.1 | ||||||
| Macro-bend loss (1625nm) | dB | 30mm radius,100turns, ≤0.1 | ||||||
| Geometric Performance | ||||||||
| Mode field diameter at 1310nm | μm | 9.2±0.5 | ||||||
| Cladding diameter | μm | 125±1 | ||||||
| Core/Cladding Concentricity Error | μm | ≤0.6 | ||||||
| Cladding Non-Circularity | % | ≤1 | ||||||
| Coating diameter(uncolored) | μm | 243±7 | ||||||
| Cladding/Coating Concentricity Error | μm | ≤12.5 | ||||||
| Mechanical Performance | ||||||||
| Proof test level | % | ≥1.0 | ||||||
| Fiber Strength | 10m, Weibull lowest probability level:2.76GPa(15%) | |||||||
| Dynamic corrosion parameter nd | ≥20 | |||||||
| Curl radius | m | ≥4 | ||||||
| Strip force | Average value | N | 1~5 | |||||
| Peak value | 1.3~8.9 | |||||||
| Environmental Performance | ||||||||
| Temperature performance(-60~+85ºC) | Additional attenuation ≤0.05dB/km is allowed at 1310nm and 1550nm. | |||||||
| Immersing performance(23±2ºC, 30days) | ||||||||
| Humidity and heat performance (85±2ºC,humidity degree over 85%,30days) | ||||||||
| Heat aging performance(85±2ºC, 30days) | ||||||||