1mm Kevlar Short Fiber for Silica Gel Resin Reinforcement

Min.Order: 1

Product origin: Shenzhen, Guangdong, China

Infringement complaint:

Complaint

US$ 20 ~ 25

Description

1mm Kevlar Short Fiber for Silica Gel Resin Reinforcement

1mm para-aramid fiber chopped strands was chopped in 1mm by a special cutting machine.This fiber has high strength and modulus,strong hydrogen bonding strength,strength up to 28 g/d or more,strength is 5-6 times of steel wire.specific modulus 2-3 times of it,toughness 2 times of it while weight is just 1/5 of the wire.Continuous using temperature range is extremely wide,long running in the range of -196 ºC to 204 ºC,no decomposition and melting at high temperature of 560 ºC,strength can maintain 75% through 100 hours at 200 ºC,also has good chemical solvent resistance,resisting acid and alkali, anti-aging,good adhesion to rubber.Usually it is used as a reinforcing material in the fields of thermoplastics,thermosetting plastics,rubber,silica gel,high-temperature composite structures,brake pads,clutch linings,friction material,wear-resistant filler,cable sheathing,gaskets,slot insulation,phase insulation barrier,interturn insulation and so on.

SPECIFICATIONS:

Model:	XGPF1201
Color:	yellowish
Fiber type:	Para-aramid
Density(g/cc)	1.47
Linear density of mono filament(D)	1.5
Filament diameter(μm)	12
Fiber length(mm)	1.0
Tensile strength( cN/dtex)	19.4-21
Elongation at break(%)	2.5-3.84
Tensile modulus(GPa)	80~120
Shrinkage(%)	<0.2(190ºC×15m)
Moisture (%):	<0.2

APPLICATION FIELDS:
1.Engineering Plastics,thermosetting resin,friction materials,automotive brakes,composite materials and Kevlar reinforced paper.
2.reinforcing materials,construction,rubber,reinforced cable,cable and other high-intensity rope.
3.composite material with resin or rubber,can significantly reduce the weight,increase loading weight,suitable for the production of aerospace equipment,high-speed trains and yachts shell.
4.Friction and sealing materials,friction materials reinforced fiber, significantly improved wear resistance,suitable for high temperature conditions.

STORAGE:
The P-aramid fiber chopped strands should be keep dry in their original bags and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire.