Overpressure sintering tungsten carbide plates have excellent red toughness,high hardness,good wear resistance,high elasticmodulus,high strength,good chemical stability,acid,alkali,high temperature oxidation,Low impact toughness,low expansion coefficient,thermal conductivity,the characteristics of the conductive similar to iron and other alloy.
1. having all kind sizes for your choose,can suply less than 400mm length.
2. Sintere by vacuum sintering furnace and HIP machine with excellent specifications without any hole.
3. suply blank plate with tolerance(-0.15~+0.15)or (0~+0.3).
4. can grinding and polishing the side and blading.
5. delivery time is 12 days.
Customization Support
| Grades | YS2T |
| Density(g/cm3) | 14.25 |
| Hardness(HRA) | ≥92 |
| T.R.S(Mpa) | ≥2400 |
| Parameter(mm) | 5mm*100mm*100mm |
| Length(mm) | 100mm |
| Type | H6 Grinding |
| grade | Density (g/cm³) | T.R.S(Mpa) | Hardness HRA | performance& application recommended | Equivalent to ISO |
| YG6 | 14.8 | 2150 | 90.0 | High wear resistance,used for processing hard wood,original wood,aluminum section bar,brass rod and cast iron. | K20 |
| YG6A | 14.9 | 1860 | 92.0 | Better wear resistant than YG6,used for processing hard wood,original wood,aluminum section bar,brass rod and cast iron. | K10 |
| YG8 | 14.8 | 2320 | 89.5 | Wear and perussion resistance,used for processing hard wood,soft wood,ferrous and non-ferrous | K30 |
| YS2T | 14.6 | 2350 | 92.0 | Fine grain carbide with high wear resistance,high bending strength ,high resistance to bonding and high thermal strenght.apply to machining refractory alloys/stainless steel and high manganness steel ect. | M10 |
| YS25 | 13.8 | 2200 | 91.0 | Carbide grade with high hardness and good wear-resistance,suitable for rough turning,milling and planing of carbide steel,cast steel,high intensity steel and steel alloy | P25 |
| YL10.2 | 14.5 | 2150 | 92.2 | Wear resistance and strength comparatively higher,suitable for processing castiron,non-ferrous,and non-metal materials | / |