E71t-11 X. 035 X 10lb Spool Gasless Flux Core Welding Wire 0.8mm 0.9mm 1.0mm 1.2mm MIG Welding Rod

Min.Order: 1,000

Product origin: Wenzhou, Zhejiang, China

Infringement complaint:

Complaint

US$ 1.5 ~ 1.9

Description

Wenzhou Tinayu Electronic Co., Ltd.

High Quality CO2 Gas shielded flux-cored welding wire

Model No: E71T-11, E71T-GS, E71T-1
Conforms to: AWS A5.20/ASME SFA A5.20
Diameter::0.8 0.9 1.0 1.2 1.6mm
Free sample OEM approved
Weld Process: Mig Welding Process
Application: for all position
Brand: Tyue

Product Description:
E71T serie sis a kind of TI type flux cored wire for CO2 welding. It has high cladding efficiency, good welding technical performance in all-position welding, apply for low carbon steel and 500MPA grade strength steel welding, such as Industry of Metallurgical, Building, Chemical, shipping, pressure vessels, mechanical equipments.

Packing & Delivery: AWS A5.20 E71T-1C, E71T-11, E71T-GS
Size(MM) × Weight (KG)
0.8MMX1KG/SPOOL,
0.8MMX5KG/SPOOL,
0.8MMX15KG/SPOOL,

0.9MMX1KG/SPOOL,
0.9MMX5KG/SPOOL,
0.9MMX15KG/SPOOL,

1.0MMX1KG/SPOOL,
1.0MMX5KG/SPOOL,
1.0MMX15KG/SPOOL,

1.2MMX1KG/SPOOL,
1.2MMX5KG/SPOOL,
1.2MMX15KG/SPOOL,

Advantage
• All-position with stable arc less splash
• Less welding smoke, shaped good appearance, high welding efficiency
• Inherent quality stable and reliable,good mechanical property of deposited metal
• Manufactured under a quality system certified to ISO 9001 requirements

Chemical Date of E71T-11

Mechanical Properties of Deposited Metal of E71T-11
Test Item	Rm(MPa)	ReL or Rp0.2(Mpa)	A(%)	KV2(J)
Guarantee Value	≥480	≥400	≥22	≥27(-20°C)
General Result	580	480	27	128

Chemical Composition of Deposited Metal (%)(CO2Shielding Gas) of E71T-11
Chemical Composition	C	Si	Mn	P	S	Ni	Cu
General Result	0.12	0.04	0.70	0.014	0.011	0.28	0.12

Chemical Date of E71T-GS

Mechanical Properties of Deposited Metal of E71T-GS
Test Item	Rm(MPa)	ReL or Rp0.2(Mpa)	A(%)	KV2(J)
Guarantee Value	≥480	≥400	≥22	≥27(-20°C)
General Result	580	480	27	128

Chemical Composition of Deposited Metal (%)(CO2Shielding Gas) of E71T-GS
Chemical Composition	C	Mn	Si	S	P	Ni	Cu
General Result	0.07	0.59	0.06	0.008	0.014	0.25	0.15

NOTE ON USAGES:Do not use shielding gas

Forward

Related products

E71t-11 X. 035 X 10lb Spool Gasless Flux Core Welding Wire 0.8mm 0.9mm 1.0mm 1.2mm MIG Welding Rod

US$ 1.5 ~ 1.9

Flux Cored Welding Wire Carbon Steel Rod E71t-11, E71t-1c, E71t-GS MIG Welding Wire

US$ 1.5 ~ 1.9

E71t-11 E71t-GS Flux Cored Gasless Welding Wire 1kg 0.7kg 0.45kg No Gas Self Shielded Flux Core Wire E71t-11 E71t-GS 0.030/0.035/0.040'' 0.8/0.9/1.0mm

US$ 1.5 ~ 3