Model | Type | 25ºC pa.s Viscosity | Min Gel Time | Non-volatile | MPa Tensile Strength | Elongation | MPa Flexural Strength | HDT ºC |
191DC-G | DC | 0.20-0.45 | 6.0-12.0 | 68-74 | 58 | 2.9 | 93 | 85 |
DC191 | DC | 0.20-0.45 | 6.0-12.0 | 68-74 | 58 | 2.9 | 93 | 85 |
191 | PA | 0.25-0.45 | 9.0-17.0 | 61-70 | 60 | 3.5 | 112 | 70 |
9196 | DC | 0.25-0.45 | 5.0-18.0 | 68-75 | 50 | 2 | 90 | 85 |
196 | PA | 0.25-0.45 | 9.0-17.0 | 61-67 | 60 | 1.8 | 113 | 66 |
196F | PA | 0.25-0.45 | 9.0-17.0 | 61-67 | 60 | 1.8 | 111 | 66 |
5118F | ISPA | 0.35-0.80 | 5.0-13.0 | 63-71 | 60 | 2.3 | 110 | 70 |
199 | ISPA | 0.35-0.65 | 10.0-16.0 | 56-64 | 55 | 1.8 | 90 | 120 |
199X | PA | 0.35-0.65 | 13.0-19.0 | 56-62 | 60 | 2 | 90 | 115 |
3301 | ABPA | 0.35-0.58 | 5.8-10.7 | 56-62 | 55 | 2 | 105 | 100 |
197 | ABPA | 0.40~0.50 | 10~25 | 47~53 | 60 | 2 | 90 | 115 |
Item | Range | unit | Testing method |
appearance | Light yellow viscous liquid | - | GB/T 8237.4.1.1 |
Acid value | 25-30 | mgKOH/g | GB/T 2895 |
Viscosity,25ºC | 0.25-0.45 | Pa.s | GB/T 7193.1 |
Solid content | 61-70 | % | GB/T 7193.3 |
Gel time ,25ºC | 9-17 | min | GB/T 7193-2008 |
Item | Unit | Measured value | Testing method |
Barco hardness | -- | 41 | GB 3854-83 |
Heat distortion temperature | ºC | 70 | GB 1634-04 |
Bending strength | MPa | 112 | GB/T 2570-95 |
Tensile Strength | MPa | 60 | GB/T 2568-95 |
Elongation at break | % | 3.5 | GB/T 2568-95 |
Impact strength | KJ/m2 | 10.2 | GB/T 2571-95 |
Item | Unit | Measured data | Testing method |
Bending strength | MPa | 365 | GB/T1449-83 |
Tensile Strength | MPa | 290 | GB/T1447-83 |