Long Carbon Chain Nylon Engineering Plastics Polyamide PA1010 Resin for Cable Electronics and Automotive Componen

 

TYPICAL PROPERTIES	CONDITION	STANDARD	UNIT	VALUE
PHYSICAL PROPERTIES
Density		ISO 1183	[g/cm³]	1.05
Moisture absorption	T=23°C / 50%RH	ISO 62	[%]	0.5
Mold shrinkage parallel	long.	ISO 294	[%]	1.0
Mold shrinkage transverse	trans.	ISO 294	[%]	1.3
RHEOLOGICAL
Viscosity number		ISO307	[ml/g]	2.4
MECHANICAL PROPERTIES
Tensile modulus	1 mm/min	ISO 527	[MPa]	1600
Tensile stress at break	50 mm/min	ISO 527	[MPa]	60
Tensile strain at break	50mm/min	ISO 527	[%]	200
Flexural strength	2 mm/min	ISO 178	[MPa]	60
Flexural modulus	2 mm/min	ISO 178	[MPa]	1200
Charpy notched	+23 °C	ISO 180/1A	[kJ/m²]	10
Charpy notched	- 30 °C	ISO 180/1A	[kJ/m²]	9
Shore hardness(D)		ISO 868		75
THERMAL PROPERTIES
Heat Deflection Temperature	0.45MPa	ISO 75	[°C]	155
Melting point	DSC	ISO 11357	[°C]	202
BURNING BEHAVIOUR
Flammability(UL94)	0,8 mm	ISO 1210	[Class]	HB
Burning rate (FMVSS)		FMVSS 302	[mm/min]

 
Polyamide 1010 (PA1010) is a translucent, light and hard, bright surface crystalline white or slightly yellow particles, relative density and water absorption than PA6, PA66 lower, high mechanical strength, impact toughness, wear resistance and self-lubrication good, has good sound attenuation; Good chemical resistance, non-toxic, insoluble in hydrocarbons, esters and low alcohols, concentrated sulfuric acid; Resistance to mold, bacteria and insects, with good electrical insulation; The melt has good fluidity and is easy to form, but the melt temperature range is narrow, and it is easy to be oxidizing and degraded. When it is higher than 100ºC, it will gradually show yellowish brown in contact with oxygen for a long time, and its mechanical strength will decrease.
 

High mechanical strength	Good impact toughness
Wear resistance and self-lubrication	Good noise reduction
Good oil resistance	Alkali resistance
Chemical resistance	Insoluble in hydrocarbons
Esters and lower alcohols	Resistant to mold
Bacteria and Moth-eaten	Good electrical insulation
Good melt fluidity, easy to form

 

Widely used in automobile, instrument, brush making, shipbuilding, printing and dyeing, textile, railway, mining, oil, household appliances and other fields.

Building Material Industry	Marble Slab , Abrasive Brush
Automotive Industry	Oil Tube
Petroleum Industry	High Pressure Tube
New Energy Source Industry	Solar Energy, Power Generation
Electronics&Electrical Industry	5G Communication
Smart Wearable	Shoe Material, Shoe Arch
Aerospace	UAV(Unmanned Aerial Vehicle)
Consumption Industry	Wiring Harness
Personal Articles Industry	Toothbrush

    PA1010 plastic products can replace metal and non-ferrous metals to make a variety of mechanical parts, motor parts and high pressure seals. Such as injection molding gear can be used as instruments, textile, automotive and printing and other mechanical equipment accessories, but also for bearing ball bracket, shaft sleeve, small worm reducer, oil pipeline and cable sheath and film, powder for metal surface anti-corrosion, wear-resistant coating.
    Long carbon chain nylon has the characteristics of corrosion resistance, pressure resistance, oil resistance, cold resistance, small expansion coefficient of fuel and so on. It is an ideal material for the manufacture of automobile tubing. 60-70% of long carbon chain nylon in developed countries is used in the production of automotive hoses, such as brake tubes, pipelines, clutch hoses, etc. Long carbon chain nylon can also be used for silencing gears, bearings, thrust pads, seismic components, wipers and so on.

(For Reference Only)
PA1010 raw materials should be dried in the oven at about 90ºC before processing. Molding products can be processed by Injection Molding, Extrusion Blow Molding and Spraying.
(1) Temperature of extrusion cylinder: the feeding section is about 160 ° C, the homogenizing section is about 215 ° C, and the molding mold is 180~190 ° C.
(2) When injection molding, the barrel temperature is 190~230 ° C, the nozzle temperature is about 205 ° C, the mold temperature is about 30 ° C, and the injection pressure is about 110MPa.
(3) After forming the product, heat it with oil or water bath (temperature about 95ºC) for 4h.
(4) When powder spraying, the raw materials should be screened with 80 mesh screens, the powder should be heated 50~60 ° C, the pre-sprayed metal parts should be preheated to 245~255 ° C, and the flame spraying method should be used (0.2~0.25MPa CO2 gas conveying powder, acetylene pressure is 0.05MPa, oxygen pressure is 0.2~0.4MPa).