Product Description:
Good resilience and aging resistance;
Low linear shrinkage and good impact fatigue properties;
Good thermal stability and weatherability (use temperature - 40 C - 250 C).
Curing conditions:
145-155ºC X 70S, actual curing time can be prolonged or shortened appropriately depending on the thickness and size of the product.
Instructions:
Use ratio is 1:100. Before use, the A. B component should be fully mixed and evenly proportioned. It can be used after vacuum defoaming treatment.
Performance parameters:
Inspection condition: Component A/B can be mixed by equal specific weight of 1:100.
Applications:
Textile products: It can be used for surface coating of cotton and linen fabrics.
Electrotechnics and Electronics: According to the applicable situation, it can be diluted to make glass fiber surface coating, and its self-extinguishing property can reach V0 grade.
| Item | Value | Standard |
| Appearance | Semi-transparent | Visual inspection |
| Density (g/cm3) | 1.09±0.01 | - |
| Hardness Shore A | 25±2 | GB/T531 |
| Tensile strength Mpa | ≥4.4 | GB/528 |
| Elongation % | ≥500 | GB/T528 |
| Tear strength KN/m | ≥13.2 | GB/T7124 |
Reminding:
Do not contact with organic substances such as N, P, S, ionic compounds such as Hg, Bi, As, and alkynes and vinyl compounds should not be allowed, to avoid poisoning of platinum catalysts and curing, especially PVC, which contains Pb, which can poison the catalysts. Some organic pigments can also cause curing to slow down or not.