High Impact Resistance of Metal Roof Antirust Paint

Min.Order: 1,000
Product origin: Shijiazhuang, Hebei, China
Infringement complaint: complaintComplaint
US$ 1.15 ~ 1.5

Description

Product Description
Acrylic Waterproof Coating(UV resistance)
Description
Color steel tile and metal roofing waterproof coating is a special waterproof coating for metal structures prepared by liquid high-quality acrylic cool and silane copolymer elastic emulsion, a variety of additives, UV-reflective materials, etc.. Waterproof system has excellent ultraviolet reflectivity, aging resistance, low temperature flexibility. It can reduce the indoor temperature and achieve the dual role of waterproofing and energy saving. Mostly used in steel structures, roofs, machinery and equipment, containers, ships, guardrails, etc.

Features
(1)Reflecting ultraviolet rays, reducing the temperature of the base surface, aging resistance, low temperature resistance and strong service life.
(2) water-based emulsion, non-toxic and harmless, a green environmental protection and energy-saving products.
(3) coating film elongation, shrinkage and deformation of the grassroots cracking to adapt to the stronger
(4) cold construction, can add color, easy construction, easy maintenance
(5) good metal bonding, no drum, no shedding.


Package
20kg/bucket

Storage
storage temperature ≥ 0 ° C, placed in a dry place in the shade storage, freezing, sun protection, shelf life of 18 months
 
Construction instructions:
1,It is strictly forbidden to contact with oily substances, stir well before use, and can be diluted with water appropriately according to the actual demand, but generally add 0-10% of water is the best.
2, brush coating, silver coating, spraying, dipping can be, construction temperature ≥ 5 °
3, before construction should be removed from the surface oil, sand and dirt debris, loose rust, rust layer thickness of not more than 120 microns.
 
Technical Data                                         
No.ItemUnitStandardResult
1Solid Content%≥6578
2Tensile strengthMPa≥1.01.8
3Elongation at break%≥300455
4Flexibility at Low Temperature, Rod bent 180ºC, ф10mm Stick--10ºC,No CrackPass
5Water Impermeability, 0.3Mpa, 30min-ImperviousPass 
6Heating Stretch rate%≤10.7 
7Drying timeSurface Dryh≤42 
Fully dryh≤85 
8Tensile strength retention after treatmentHeat Treatment %≥80105 
Alkali Treatment%≥6095 
Acid Treatment%≥4092 
9Elongation at break after treatmentHeat Treatment %≥200326 
Alkali Treatment%≥200403 
Acid Treatment%≥200289 
 