Features
It has excellent electrical insulation performance, high and low temperature resistance, water and moisture resistance, weather resistance, ozone resistance and chemical stability, and good flexibility.
Appearance | milk-white light alowed, no mechanical impurities, light yellow to reddish brown transparent liquid. |
Solid content % | ≥55 |
Viscosity s/T-4,25ºC | 25-75 |
Drying time | ≤2h/200ºC |
Heat tolerance | >200h/200ºC |
Loss on heat 3h/250ºC,% | ≤3 |
Features and Main application | glass cloth used for the electric insulation of engines. |
Application
It is widely used as the base resin for high temperature resistant coatings and special coatings, as well as general high and low temperature resistant insulating impregnating paints, covering paints (varnishes, paints, enamels, etc.), and H-class electrical insulating materials.
Usage
1. According to the construction process, can be specified by adding diluent conditioning solid content and Viscosity. to control the thickness of the coating, usually adjusted for spraying viscosity 15-25 seconds; diluent should not contain water, sulfur and other impurities. The coating adhesive force will be affected, so was stem and other properties.
2. When in use, it should be avoided with acid and alkali, organic acids and amines contact, otherwise it will accelerate ageing, affect the performance of the product.
3. At work, according to the resin NO and the use of different requirements and then confirm dying condition, for high temperature dying type, it should be solvent dying to volatile at a lower temperature (120 or 160 ° C). Finally curing at 220 ºC.
4. Resin has good compatibility with heat resistant pigments (aluminum, glass bead, low-density ceramic powder. Black chromium oxide and iron oxide powder, etc.), the coating should be dipping, spraying, brush and other construction methods, curing the coating can be used in 250-400 ºC. Some may be resistant 500-600 ° C, even higher temperatures.
5. Application examples of reference
(1) fire-resistant insulation coating formula
silicone resin | Higher chlorinated polyethylene | epoxy resinF-644 | Polyamide resin | Padding | Flux | Titanate |
40-60Copies | 5-15Copies | 10-20Copies | 4-12Copies | 45-85Copies | 5-15Copies | 1-2Copies |
All material will be transferred into a paste, and then grinding with sand mill 20 ~ 30min after the addition of solvent dispersion, and then filter.
(2) fire-resistant aluminum section formula :
60% Methylphenyl silicone resin | 65%Aluminum Paste | xylene | Dispersant |
76Copies | 26Copies | 46Copies | 2Copies |
Put aluminum paste into a container, add a small amount of resin, stir slowly, add disperser and residual resin, added xylene to construction of viscosity after fully stirred, with 120 mesh silk filter then finish.
Safety Note
1. Resin contains flammable, explosive and toxic solvents, In the process of use and processing, should pay attention to the site operation ventilation, to prevent fire, strengthening the protection of workers.
2. During transportation and storage, prevent sunlight, fire and heat protection, pay attention to warehouse ventilation.
3. Packed with galvanized iron sheet barrel, storage period is generally 6 months, if pass storage period, please test it strictly and then use. Avoid heat, otherwise it will reduce the storage stability.