Bulk Density | 0.35-1.0 g/cm3 | Dimensional Stability | ±2% |
Shore Hardness | 30-85 D | Water Absorption | <1% |
Tensile Strength | 12-20 Mpa | Flexural Strength | 12-18 Mpa |
Elongation At Break | 15-20% | Flexural Modulus | 800-900 Mpa |
Impact Strength | 8-15 KJ/m2 | Screw Holding Strength | >800 N |
Vicat Softening Temperature | 73-76 ºC | Heating Dimensional Variation Ratio | +2% |
Hydroscopicity | ≤1% | Fire Resistance | self-extinguish within 5seconds |
Testing Item | Unit | Testing Result |
Density | g/cm3 | 0.33-1.0 |
Tensile Strength | MPa | 12-20 |
Bending Intensity | MPa | 12-18 |
Bending elasticity Modulus | MPa | 800-900 |
Impacting Intensity | KJ/m2 | 8 -15 |
Breakage Elongation | % | 15-20 |
Shore hardness D. | D | 40-90 |
Water Absorption | % | ≤1.5 |
Vicar Softening Point | °C | 73-76 |
Fire Resistance | Self-Extinguishing Less than 5 seconds |