High quality/High cost performance Excellent Rigid Long Carbon Chain Nylon Plastic Raw Material PA101

Min.Order: 1,000
Product origin: Jining, Shandong, China
Infringement complaint: complaintComplaint
US$ 5.2 ~ 13

Description

Detailed Photos

TDS Sheet

 

TYPICAL PROPERTIES
 
CONDITION
 
STANDARD
 
UNIT
 
VALUE
 
PHYSICAL PROPERTIES
 
   
Density ISO 1183[g/cm³]1.05
Moisture absorptionT=23°C / 50%RHISO 62[%]0.5
Mold shrinkage parallellong.ISO 294[%]1.0
Mold shrinkage transversetrans.ISO 294[%]1.3
RHEOLOGICAL    
Viscosity number ISO307[ml/g]2.4
MECHANICAL PROPERTIES    
Tensile modulus1 mm/minISO 527[MPa]1600
Tensile stress at break50 mm/minISO 527[MPa]60
Tensile strain at break50mm/minISO 527[%]200
Flexural strength2 mm/minISO 178[MPa]60
Flexural modulus2 mm/minISO 178[MPa]1200
Charpy notched+23 °CISO 180/1A[kJ/m²]10
Charpy notched- 30 °CISO 180/1A[kJ/m²]9
Shore hardness(D) ISO 868 75
THERMAL PROPERTIES    
Heat Deflection Temperature0.45MPaISO 75[°C]155
Melting pointDSCISO 11357[°C]202
BURNING BEHAVIOUR    
Flammability(UL94)0,8 mmISO 1210[Class]HB
Burning rate (FMVSS) FMVSS 302[mm/min] 
 

Product Description


PA1010 is made of pure green plant castor seed as raw material. Is a translucent, light and hard, bright surface of crystalline white or yellowish particles, relative density and water absorption than PA6, PA66 lower, higher than 100ºC, long-term contact with oxygen will gradually appear yellowish brown, while mechanical strength decline.


Widely used in automobile, instrument, brush making, shipbuilding, printing and dyeing, textile, railway, mining, oil, household appliances and other fields.

Physical Properties


Polyamide 1010 (PA1010) is a translucent, light and hard, bright surface crystalline white or slightly yellow particles, relative density and water absorption than PA6, PA66 lower, high mechanical strength, impact toughness, wear resistance and self-lubrication good, has good sound attenuation; Good chemical resistance, non-toxic, insoluble in hydrocarbons, esters and low alcohols, concentrated sulfuric acid; Resistance to mold, bacteria and insects, with good electrical insulation; The melt has good fluidity and is easy to form, but the melt temperature range is narrow, and it is easy to be oxidizing and degraded. When it is higher than 100ºC, it will gradually show yellowish brown in contact with oxygen for a long time, and its mechanical strength will decrease.
 
High mechanical strengthGood impact toughness
Wear resistance and self-lubricationGood noise reduction
Good oil resistanceAlkali resistance
Chemical resistanceInsoluble in hydrocarbons
Esters and lower alcoholsResistant to mold
Bacteria and Moth-eatenGood electrical insulation
Good melt fluidity, easy to form 

 

Application

Widely used in automobile, instrument, brush making, shipbuilding, printing and dyeing, textile, railway, mining, oil, household appliances and other fields.
Building Material IndustryMarble Slab , Abrasive Brush
Automotive Industry Oil Tube
Petroleum Industry High Pressure Tube
New Energy Source Industry Solar Energy, Power Generation
Electronics&Electrical Industry5G Communication
Smart WearableShoe Material, Shoe Arch
Aerospace   UAV(Unmanned Aerial Vehicle)
Consumption IndustryWiring Harness
Personal Articles IndustryToothbrush
    PA1010 plastic products can replace metal and non-ferrous metals to make a variety of mechanical parts, motor parts and high pressure seals. Such as injection molding gear can be used as instruments, textile, automotive and printing and other mechanical equipment accessories, but also for bearing ball bracket, shaft sleeve, small worm reducer, oil pipeline and cable sheath and film, powder for metal surface anti-corrosion, wear-resistant coating.
    Long carbon chain nylon has the characteristics of corrosion resistance, pressure resistance, oil resistance, cold resistance, small expansion coefficient of fuel and so on. It is an ideal material for the manufacture of automobile tubing. 60-70% of long carbon chain nylon in developed countries is used in the production of automotive hoses, such as brake tubes, pipelines, clutch hoses, etc. Long carbon chain nylon can also be used for silencing gears, bearings, thrust pads, seismic components, wipers and so on.

Plastic Product Molding Method

(For Reference Only)
PA1010 raw materials should be dried in the oven at about 90ºC before processing. Molding products can be processed by Injection Molding, Extrusion Blow Molding and Spraying.

(1) Temperature of extrusion cylinder: the feeding section is about 160 ° C, the homogenizing section is about 215 ° C, and the molding mold is 180~190 ° C.
(2) When injection molding, the barrel temperature is 190~230 ° C, the nozzle temperature is about 205 ° C, the mold temperature is about 30 ° C, and the injection pressure is about 110MPa.
(3) After forming the product, heat it with oil or water bath (temperature about 95ºC) for 4h.
(4) When powder spraying, the raw materials should be screened with 80 mesh screens, the powder should be heated 50~60 ° C, the pre-sprayed metal parts should be preheated to 245~255 ° C, and the flame spraying method should be used (0.2~0.25MPa CO2 gas conveying powder, acetylene pressure is 0.05MPa, oxygen pressure is 0.2~0.4MPa).