Ka402 2-3mm Water Purification Activated Alumina Ball

Min.Order: 1,000

Product origin: Pingxiang, Jiangxi, China

Infringement complaint:

Complaint

US$ 0.99 ~ 1.65

Description

KA402 2-3mm Water Purification Activated Alumina Ball

Activated Alumina, there are many micro-paths, so the specific surface is large. Zhongci Activated Alumina, the defluorinate effect is good. The capacity is stable. It has high strength, low abrasion, no soften in water, no expansion, no powdery no crack. It can widely used in the deep drying of cracked gas, ethylene, hydrogen-generation, air separation, instrument air drying and fluorin treatment for water, also in the absorbing pollution material, such as H2S, SO2, HF and paraffin in the waste gas, especially in the drinking water defluorinate.

Activated Alumina is an excellent desiccant for drying a wide variety of liquids and gases. It's high attrition resistance and crush strength. It has larger water adsorption capacity comparing to molecular sieve at high relative humidity and providing long service life with performance at or below dew point specifications. Activated alumina is widely used in large and small dryers. It is appropriate for use in dehydrating gases in both thermally regenerative and pressure swing adsorption (PSA) process.

Typical Chemical Formula: Al₂O₃·nH₂O (0≤n≤0.8).

Technical Parameter:

Model		Activated Alumina
Color		White
Shape		Sphere
Type		KA401	KA402	KA403	KA404	KA405
Crystal Type		X-p	X-p	Y	Y	X-p
Chemical Composition	Al₂O₃ Content (%)	≥93	≥93	≥93	≥93	≥93
Chemical Composition	Na₂O Content (%)	≤0.3	≤0.3	≤0.5	0.15-0.3	≤0.3
Physical properties	Bulk density (g/ml)	0.68-0.72	0.70-0.75	0.65-0.75	0.70-0.80	0.72-0.78
	Pore volume (ml/g)	0.30-0.45	0.30-0.42	0.40-0.46	0.40	0.30-0.50
	Surface area (m²/g)	≥300	≥300	260-300	≥300	≥300
	Active (%)	/	/	56-62	/	/
	Attrition loss (%)	≤1.0	≤1.0	≤1.0	≤0.4	≤0.8
	LOI (%)	≤8	≤8	≤8	≤5	≤8
	Static absorption (%) (RH=60%)	Water Absorption	Fluorin Absorption	Water Absorption	Water Absorption	Water Absorption
	Static absorption (%) (RH=60%)	17-19	0.2-0.3	50	50-70	17-19
Crushing Strength (N/PC)	Φ1-2 (mm)	≥40	≥40	/	/	/
	Φ2-3 (mm)	≥70	≥70	/	/	/
	Φ3-5 (mm)	≥120	/	≥120	≥120	≥120
	Φ4-6 (mm)	≥150	/	≥150	≥150	≥150
	Φ5-7 (mm)	≥200	/	/	/	≥200
	Φ6-8 (mm)	≥300	/	/	/	≥300
	Φ12-14 (mm)	≥350	/	/	/	/