430G/M2 600G/M2 1200G/M2 Fire Proof E Fiberglass Cloth, Heat Insulation Fire Resistant Glass Fiber Cloth, PU Silicone Rubber Coated Steel Wire Reinforced Cloth

Min.Order: 100
Product origin: Qingdao, Shandong, China
Infringement complaint: complaintComplaint
US$ 0.21 ~ 0.96

Description
Product Description

E-Glass Fiberglass Fabric also called fiberglass fabric which is an engineering material, which has the excellent merit such as anti-burns, anti-corrosion, stable-size, heat-isolation, minimum elongated shrinkage, high intensity, this new material product has already covered many domains such as electric appliances, electronic, transportation, boat building, FRP products, chemical engineering, architectural engineering, heat insulation, sound absorption, fire prevention and environmental protection, etc.

Fiberglass Fabric has: plain weave, twill weave, satin weave, gauze weave.
A).Plain weave: it can be used in electricity insulation materials and reinforced materials in industry, because of inseparable structure, plain and clear lines. 100gsm-800gsm
B).Twill weave: compared with plain weave, it is of high density, high intensity, with a soft and loose structural weave. It can be used in ordinary reinforced materials, filter materials, and painting cloth.
C) Satin weave: compared with plain weave and twill weave, it is of high density,high intensity, with a soft and loose structural weave with a good texture. It is applicable for use as a higher reinforced material in machinery.
D).Gauze weave: said lattice twist weave. It can be used in spread model curtain,resin reinforced emery wheel gray cloth and lattice embed belt. 

Product Parameters

Specifications

ItemWeaveWeight (g/m2)ThicknessWidthRoll LengthColor
E/C 01Plain105 ± 50.1mm0.9-2.2m300mwhite
E/C 012Plain120 ± 50.12mm0.9-2.2m300mwhite
E/C 014Plain140 ± 50.14mm0.9-2.2m300mwhite
E/C 016Plain160 ± 50.16mm0.9-2.2m300mwhite
E/C 018Plain180 ± 50.18mm0.9-2.2m300mwhite
E/C 260Plain260 ± 50.25mm0.9-2.2m200mwhite
E/C 320Plain340 ± 50.30mm0.9-2.2m100mwhite
E/C 7628Plain200 ± 50.18mm0.9-2.2m100mwhite
E/C 3732Twill430 ± 50.43mm0.9-2.2m100mwhite/yellow
E/C 600Plain Pane600 ± 50.55mm0.9-2.2m50mwhite/yellow
E/C 3784Satin840 ± 50.80mm0.9-2.2m50mwhite/yellow
E/C 3788Satin1750 ± 51.65mm0.9-2.2m50mwhite/yellow


Knitted Fiberglass Fabric:

Knitted Fabric reinforcements provide customized fiber placement and design flexibility to increase part strength and durability.

Knitted Fabric reinforcements are produced on large looms where fibers are directionally oriented (X and Y axis, or sometimes referred to as the 0°, 90° and 45° orientation) in multiple layers and then stitched together to keep the fibers in place. The resulting fabric is trimmed and rolled. This production process allows for a multitude of fiber orientation patterns, thickness, weight distribution and the incorporation of different types of reinforcements like carbon fiber or aramid fiber. Fabrics can be balanced, with the same amount of fiber used in both the X and Y axis or unbalanced with added fiber in one axis to provide more reinforcement strength in that direction. Using knitted fabrics allows for significant part or laminate design flexibility and is widely used in boat building, transportation, wind blades and recreational products where specific strength orientation in the laminate is optimal.

Product No.Overall Density(g/m2)+45°Roving Density(g/m2)-45°Roving Density(g/m2)Chop Density(g/m2)Polyester Yarn Density(g/m2)
HTDX1601728080/6
HTDX240233106106/6
HTDX300306.7150.33150.33/6
HTDX400407200.5200.5/6
HTDX450457225.5225.5/6
HTDX600607.2300.6300.6/6
HTDX800807.6400.8400.8/6
HTDX12001208.6601.3601.3/6
HTDXM400/225632200.5200.52256
HTDXM600/225832.2300.6300.62256
HTDXM800/4501257.6400.8400.84506
HTDXM1208682200.5200.52756
HTDXM1308732225.5225.52756
HTDXM1708882.2300.6300.62756
HTDXM24081082.6400.8400.82756

 


High Temperature Proof Fiberglass Fabric

Thicker, heavier and stronger. Provides better durability light and far more resistance to heat impact from welding sparks as compared to other thinner and textured clothes. Non hairy texture preventing irritation to be exposed skin common in other fabric and asbestos clothes. Reduce the overall impact temperature and prevent burn through.

Temperature resistance capability of up to 550°C and can sustain even higher temperature sparks intermittently. Provides better durability, when subjected to heat shock treatments, Soft and flexible, making it ideal for wrapping around uneven surfaces and equipments.


High Silica Fiberglass Fabric

High silica fiberglass is inorganic fiber which contents more than 96% of SiO2. It is materials of high temperature resistance for fireproof protective cloth, fireproof curtain, fire blanket, protective materials for welding, filter for molten metal, dust collecting in media of high temperature gas and filtration in media of high temperature liquid,etc.

High temperature properties:

Soft point nearly 1700 deg, It can work 10 minutes at 1450 deg

Keep good state at 1600 deg for 15 seconds.
 

Long period service at 1000 deg for working temperature.
 

Excellent ability: low thermal conductivity, good chemical stability,

Good electric insulation, low thermal shrinkage.

Product CodeWeaving StyleWeight(gsm)Thicness(mm)Silica Content(%)Working Temperature
HS4004HS400±300.38±0.05≥961000ºC
HS6008HS600±300.7±0.05≥961000ºC
HS110012HS1100±301.3±0.05≥961000ºC
 


Silicone Rubber Coated Fiberglass Fabrics:
 

Silicone Coated Fiberglass Fabric is constructed from a fiberglass base cloth and impregnated or coated one side or both sides with a specially compounded silicone rubber. Due to silicone rubber physiological inert, not only increase the strength, thermal insulation, fireproof , insulating properties, but also has the ozone resistance, oxygen aging, light aging, climate aging , oil resistance and other properties. 

SIlicone Rubber coated fiberglass cloth is a fiberglass cloth, which possesses the properties of temperature resistance, anti-corrosion, high strength and made by rolling or impregnation with organic rubber. It is a newly made product with properties and many uses.

 

ITEM
Thickness

(mm)
Woven
Fabric weight

(g/m²)
Coating weight

(g/m²)
HTD-200 C 80
0.23
Plain
200
80
HTD-430 C 80
0.43
Twill
430
80
HTD-430 C 140
0.45
Twill
430
140
HTD-430 C 160
0.46
Twill
430
160
HTD-566 C 200
0.6
Twill
560
200
HTD-566 C 240
0.62
Twill
560
240
HTD-566 C 300
0.65
Twill
560
300
HTD-840 C 200
0.85
Stain
840
200
HTD-840 C 280
1.0
Stain
840
280
HTD-1050 C 750
1.1
Stain
1050
750
HTD-1650 C 850
1.5
Stain
1650
850
HTD-1800 C 2000
2.5
Stain
2000
2000


Polyurethane (PU) coated Fiberglass Fabric is made of fiberglass which is woven by high quality E-glass filament yarns, and then coated with Polyurethane (PU) on single side or both sides, finally colored with aluminum pigments.

It features good rebound resilience, toughness, softness,good abrasion & allergen resistance, oils resistance, cold,aging and weather resistance,and anti-solvents, and water proof.it can withstand temperature up to 180ºC for short bursts,this kind of cloth has lots of positive properties,bright in color,  It also has the function of an anti bacterium,and can also be used for mould proofing, heat-insulation and anti-ultraviolet.

Polyurethane 1 side Coating style Glass Fiber Fabric
Inspection item
Technical index
Weight
460g/m2
620g/m2
690g/m2
690g/m2
1070g/m2
Thickness
0.4mm
0.77mm
0.63mm
0.7mm
1.2mm
Temperature resistance
-50ºC~180ºC
Color
Green,Silver
Fabric style
Fiberglass with steel reinforced,Fiberglass
Fire resistance
Non-flammable(NF92507,M0)
Applications
Insulation jackets,mattress and Pad,fabric expansion joints,fabric ductwork connector,fire doors&fire curtains,welding/fire blankets.
Polyurethane both side Coating style Glass Fiber Fabric
Inspection item
Technical index
Weight
220g/m2
460g/m2
640g/m2
720g/m2
720g/m2
880g/m2
Thickness
0.21mm
0.4mm
0.86mm
0.7mm
0.72mm
0.9mm
Temperature resistance
-50ºC~180ºC
Color
Red/white color,yellow/green color,grey/white color,blue/black color,silver grey color,white,red,black,yellow,blue,green,silver grey
Fabric style
Fiberglass with steel reinforced,fiberglass
Fire resistance
Non-flammable(NF92507,M0)
Applications
Insulation jackets,mattress and Pad,fabric expansion joints,fabric ductwork connector,fire doors&fire curtains,welding/fire blankets
 

Storage

Storage

Unless otherwise specified, the fiberglass products should be in dry, cool and moisture-proof area. The room temperature and humidity should be always maintained at 15ºC~35ºC and 35%~65%. It is best if the product is used within 12 months after production date. The fiberglass products should remain in their original packaging until just prior to user.

Application




FAQs

1. What is your terms of packing?
    Generally, we pack our goods in carton with pallet

2. What is your tems of payment?
    T/T 30% as deposit, and 70% before delivery. We'll show you the photos of the products and packages before you pay the balance.

3. What is your terms of delivery?

    EXW, FOB, CFR, CIF,L/C at sight

4. How about your delivery time?

    Generally, it will take 21 days after receiving your advance payment. The specific delivery time depends on the items and the quantity of your order.

5. Can you produce according to the samples?
   
Yes, we can produce by your samples or technical drawings. We can build the molds and fixtures.

6. What is your sample policy?
    We can supply the sample if we have ready parts in stock, but the customers have to pay the sample cost and the courier cost.

7. Do you test all your good before delivery?
    Yes, we have 100% test before delivery

 
 
          24 Hours Services         
Choose us, you will get the key of market!
Contact us, we will use the professional knowledge serve you!