| Dimensions (mm) | Dimensions (inch) | Pouring Rate (kg/s) | Filtration Capacity (ton) | |
| 178×178×50 | 7×7×2 | 0.2-0.6 | 5 | |
| 228×228×50 | 9×9×2 | 0.3-1.0 | 10 | |
| 305×305×50 | 12×12×2 | 0.8-2.5 | 15 | |
| 381×381×50 | 15×15×2 | 2.2-4.5 | 25 | |
| 430×430×50 | 17×17×2 | 3.0-5.5 | 35 | |
| 508×508×50 | 20×20×2 | 4.0-6.5 | 45 | |
| 585×585×50 | 23×23×2 | 5.0-8.6 | 60 |
| Dimensions (mm) | Pouring Rate (kg/s) | Filtration Capacity (kg) | |||
| Grey Iron | Ductile Iron | Grey Iron | Ductile Iron | ||
| 40×40×22 | 4 | 3 | 65 | 32 | |
| 50×50×22 | 6 | 4 | 100 | 52 | |
| 75×50×22 | 9 | 6 | 150 | 75 | |
| 75×75×22 | 14 | 9 | 220 | 100 | |
| 100×50×22 | 12 | 8 | 200 | 100 | |
| 100×75×22 | 18 | 12 | 300 | 150 | |
| 100×100×22 | 25 | 16 | 400 | 200 | |
| 150×150×22 | 50 | 36 | 900 | 450 | |
| Dimensions (mm) | Zirconia Foam Filter | Dimensions (mm) | Magnesia Foam Filter | ||
| Pouring Rate(kg) | Filtration Capacity(kg) | Pouring Rate(kg) | Filtration Capacity(kg) | ||
| 50×50×22 | 3~5 | 30 | Ф50×22 | 4.0 | 60 |
| 50×75×22 | 4~6 | 40 | Ф60×22 | 7.0 | 80 |
| 75×75×22 | 7~12 | 60 | Ф90×22 | 10.0 | 120 |
| 75×100×22 | 8~15 | 80 | Ф120×22 | 16.0 | 160 |
| 100×100×22 | 14~20 | 100 | 100×100×22 | 13.0 | 140 |
| Ф50×22 | 2~6 | 18 | 150×150×25 | 22.0 | 260 |
| Ф80×22 | 6~10 | 50 | 230×230×30 | 130.0 | 3100 |
| Ф90×22 | 8~16 | 70 | 300×300×40 | 260.0 | 5200 |
| Material | Alumina | Silicon Carbide | Zirconia |
| Color | White | Grey black | Yellow |
| Pore Density | 10-60ppi | 10-30ppi | 10-30ppi |
| Porosity | 80-90% | 80-90% | 80-90% |
| Refractoriness | ≤1100ºC | ≤1500ºC | ≤1700ºC |
| Bending Strength | >0.6Mpa | >0.8Mpa | >1.0Mpa |
| Compression Strength | >0.8Mpa | >0.9Mpa | >1.2Mpa |
| Volume-weight | 0.3-0.45g/cm3 | 0.35-0.5 g/cm3 | 0.9-1.5 g/cm3 |
| Thermal shock resistance | 6 times/1100ºC | 6 times/1100ºC | 6 times/1100ºC |
| Application | Aluminium, Aluminium alloys and other Non-ferrous alloys | Ductile Cast Iron, Malleable Cast Iron, Gray iron and other Cast Iron | High melting point metal alloys like Steel, Alloy Steel, Stainless Steel etc |
| Chemical Composition | Al3O2> 80% SiO2< 10% | SiC≥60% Al2O3≤30% SiO2≤10% | ZrO2≥ 94% Al2O3≤1.8% MgO≥3.0% SiO2≤0.5% Fe2O3≤0.10% |