Jushi 2400tex Fiberglass Direct Roving for Woven Roving Products

Min.Order: 1,000

Product origin: Jiujiang, Jiangxi, China

Infringement complaint:

Complaint

US$ 0.59 ~ 0.75

Description

Direct Roving For Filament Winding

Direct Roving for Filament winding, is compatible with unsaturated polyester, polyurethane, vinyl ester, epoxy and phenolic resins.

Filament Winding Process
Traditional Filament Winding
In the filament winding process , continuous strands of resin-impregnated glassfiber are wound under tension onto a mandrel in precise geometric patterns tobuild up the part which is then cured to form the finished parts.

Continuous Filament Winding
Multiple laminate layers , composed of resin , reinforcement glass and other materials are applied to a rotating mandrel , which is formed from a continuous steel band continuously traveling in a cork-screw motion . The composite part is heated and cured in place as the mandrel travels through the line and then cut into a specific length with a traveling cut-off saw .

Good process performance and low fuzz
Compatibillty with multiple of resin systems
Good mechanical properties
Complete and fast wet-out
Excellent acid corrosion resistance

Item	Linear Density	Resin Compatibility	Features	End Use
BHFW-01D	1200,2000,2400	EP	Compatible with epoxy resin, designed for filament winding process under high tension	used as reinforcement to manufacture high pressure pipe for petroleum transmission
BHFW-02D	2000	Polyurethane	Compatible with epoxy resin, designed for filament winding process under high tension	Used to manufacture utility rods
BHFW-03D	200-9600	UP,VE,EP	Compatible with resins; Low fuzz; Superior processing property; High mechanical strength of the composite product	Used to manufacture storage tanks and medial-pressure FRP pipes for water transmission and chemical corrosion
BHFW-04D	1200,2400	EP	Excellent electrical property	Used to manufacture hollow insulation pipe
BHFW-05D	200-9600	UP,VE,EP	Compatible with resins; Excellent mechanical properties of the composite product	Used to manufacture normal pressure-resistant FRP pipes and storage tanks
BHFW-06D	735	UP,VE,UP	Excellent process performance; Excellent chemical corrosion resistance, such as crude oil and gas H2S corrosion etc; Excellent abrasion resistance	Designed for RTP (reinforcement thermoplastics pipe) filament winding which requires acid resistance and abrasion resistance. It is suitable for application in spoolable piping systems
BHFW-07D	300-2400	EP	Compatible with epoxy resin; Low fuzz; Designed for filament winding process under low tension	used as reinforcement of pressure vessel and high- and medial- pressure resistance FRP pipe for water transmission

Identification
Type of Glass	E
Direct Roving	R
Filament Diameter, μm	13	16	17	17	22	24	31
Linear Density, tex	300	200 400	600 735	1100 1200	2200	2400 4800	9600

Technical Parameters
Linear Density (%)	Moisture Content (%)	Size Content (%)	Breakage Strength (N/Tex)
ISO1889	ISO3344	ISO1887	IS03341
±5	≤0.10	0.55±0.15	≥0.40

Main uses include manufacture of FRP pipes of various diameters, high-pressure pipes for petroleum transitions, pressure vessels, storage tanks, and, insulation materials such as utility rods and insulation tube.

Product List

Storage
Unless otherwise specified, fiberglass products should be stored in a dry, cool and rain-proof area. It is recommended that the room temperature and humidity should be always maintained at 15ºC~35ºC and 35%~65% respectively. To ensure safety and avoid damage to the product, the pallets should not be stacked more than three layers high. When the pallets are stacked in 2 or 3 layers, care should be taken to correctly and smoothly move the top pallet.
The product should be transferred to the workshop 24 hours before use to undergo conditioning.

Packaging
The product can be packed on pallet or in small cardboard boxes.

Package height mm(in)	260(10)	260(10)
Package inside diameter mm(in)	160(6.3)	160(6.3)
Package outside diameter mm(in)	270(10.6)	310(12.2)
Package weight kg (lb)	15.6(34.4)	22(48.5)

Number of layers	3	4	3	4
Number of doffs per layer	16		12
Number of doffs per pallet	48	64	36	48
Net weight per pallet kg (lb)	750(1653.4)	1000(2204.6)	792(1764)	1056(2328)