Product Introduction:
Low cement castable is a new type of castable. Due to the low CaO content in low cement castable, it can reduce the generation of eutectic phase in the material, which improves the refractoriness , High temperature strength and slag corrosion resistance of the product.Property | Unit | Value | |
Maximum Service Temperature | °C | 1590 | |
Bulk Density | g/cm3 | 1.9 - 2.6 | |
Cold Crushing Strength | Dried 110ºC | MPa | >18 >13 |
Fired at 1000ºC | |||
Modulus of Rupture | Fired at 1000ºC | MPa | >15 |
Grain Size | +355 µm | Wt % | 40 Min |
-250 µm | 50 Max | ||
Shrinkage at 110 °C after 24 hours | % | 1.5 Max | |
SiC | wt % | 84 Min | |
SiO2 | wt % | 7 - 9 | |
Al2O3 | wt % | 2 - 3 | |
Fe2O3 | wt % | < 0.4 | |
Others | wt % | 4 - 5 | |
Water Requirement | wt % | 6 |
Q1. Can I see the sample first before I place the real order ?
A1. Of course. We can offer little sample for testing quality and market.
Q2. What products can you supply ?
A2. We are specialized in refractory such as magnesite,SIC,bauxite and GPC.
Q3. Are you a manufacturer or trading company?
A3. We are a manufacturer with more than 20 years experience.
Q4. What is the delivery time?
A4. It is not fixed and depend on your order quantity.Usually, it will take 7~15 days.