Products Description:

Specifications PVC (Polyvinyl Chloride) is one of the most popular amorphous plastics. There are two kinds of PVC; one is hard type and the other is flexible or soft.
In the cable industry . Especially PVC having low temperature stability can easily stick to metallic surface when it's heated. PVC is widely used in cable industry because of its resistant for heavy weather condition, easy processing and better electrical properties.
If PVC is directly subjected to heat, HCl (hydrogen chloride) is disseminated and colour of the PVC gets yellow. Depending on the rate of corruption due to the heat, color of PVC changes to yellow, red, brown, black respectively. During the heating, all physical and chemical properties change. During the process, toxic gases disseminate and humidity are got away by vacuum. Some additional materials should also be used in production process. These are generally as followings;

PVC Formule

1. Plastiphians
2. Stabilizetor
3. Lubricant
4. Filling (bedding) compound
5. Strength modifier
6. Compounds to facilitate of process
7. Pigments

Flame retardant and optic bledcher material can also be used with above. Different type PVC granules can be produced by changing the rate of the above materials in the granule according to the requirements of application field for final product.
PVC granules are mainly used as 4 different types in the cable industry as lifted below.

Type Of PVC Granule
1. Outer sheath
2. Insulation
3. Filler
4. PVC for flexible cables

In addition above, flame retardant and other specific type of granules can be produced according to costumer requirements.

Technical specifications of 70 ºC pvc compound

Tensile Strength	MPa	20.5
Fracture Tensile Strain	%	320
Ageing Temperature	ºC	100
Ageing Time	h	168
Tensile Strength After Ageing	MPa	22.5
Max Change of Tensile Strength	%	+12
After Ageing Fracture Tensile Strain	%	290
Max Change of Fracture Tensile Strain	%	-10
Thermal Deformation	%	28
Thermal Ageing Quality Loss	g/m²	19
200ºC Thermal Stability Time	min	90
20ºC Volume Resistivity	Ω.cm	2.0*1011

Technical specifications of 90 ºC pvc compound

Tensile Strength	MPa	20
Fracture Tensile Strain	%	330
Ageing Temperature	ºC	100
Ageing Time	h	240
Tensile Strength After Ageing	MPa	21.5
Max Change of Tensile Strength	%	+8
After Ageing Fracture Tensile Strain	%	310
Max Change of Fracture Tensile Strain	%	-6
Thermal Deformation	%	28
Thermal Ageing Quality Loss	g/m²	9
200ºC Thermal Stability Time	min	120
20ºC Volume Resistivity	Ω.cm	2.0*1010

About us:
Our services:
1.Sales team can supply professional service with active attitude towards each question each requirement each issue.
2. 24 hours stand-by
3. Sample free ,but buyer need pay for freight cost

Sample:Free for the existed sample
Sample charge: 50-200usd depend on production, could be refunded after ordered
Sample production time: 5-7 days
Shipping fee: prepaid or collect

Packing & delivery details:
1.Low MOQ: It can meet your promotional business very well.
2.Terms of delivery: FOB, CIF, CRF.
3.Terms of payment : L/C, T/T, Western Union,Cash.
4.Port of Loading :Shanghai,China.
5.Time of Delivery: 3 days for samples,1x20fcl within 30work days.
6.Packing: Usually use carton with insider PE bag,or other Seaworthy Packing as required.

Forward

Related products