| Product Description | |||
| 30% Glass Reinforced, Heat Stabilized, High Flow | |||
| General | |||
| Form | Resin Pellets | ||
| Filler | 30 % Glass Fiber | ||
| Feature Good Thermal Excellent Processability | |||
| Physical | Nominal Value | Test Method | |
| Dry: Density | 1.35 g/cm³ | ISO 1183 | |
| Dry: Molding Shrinkage, Across Flow | 1.1 % | ISO 294-4 | |
| Dry: Molding Shrinkage, Flow | 0.30 % | ISO 294-4 | |
| Dry: Water Absorption, Saturation(23 °C) | 6.0 % | ISO 62 | |
| Dry: Water Absorption, Equilibrium(50% RH;23 °C) | 1.8 % | ISO 62 | |
| Mechanical | Nominal Value | Test Method | |
| Dry: Tensile Modulus | 9350 MPa | ISO 527-2 | |
| Condition: Tensile Modulus | 5700 MPa | ISO 527-2 | |
| Dry: Tensile Stress, Break | 160 MPa | ISO 527-2 | |
| Condition: Tensile Stress, Break | 105 MPa | ISO 527-2 | |
| Dry: Tensile Strain, Break | 3.0 % | ISO 527-2 | |
| Condition: Tensile Strain, Break | 7.0 % | ISO 527-2 | |
| Dry: Flexural Modulus | 8500 MPa | ISO 178 | |
| Dry: Flexural Stress | 235 MPa | ISO 178 | |
| Dry: Charpy Notched Impact Strength | ISO 179 1eA | ||
| -30 °C | 10 kJ/m² | ||
| 23 °C | 12 kJ/m² | ||
| Condition: Charpy Notched Impact Strength | ISO 179 1eA | ||
| -30 °C | 10 kJ/m² | ||
| 23 °C | 22 kJ/m² | ||
| Dry: Charpy Unnotched Impact Strength | ISO 179 1eU | ||
| -30 °C | 65 kJ/m² | ||
| 23 °C | 85 kJ/m² | ||
| Condition: Charpy Unnotched Impact Strength | ISO 179 1eU | ||
| -30 °C | 65 kJ/m² | ||
| 23 °C | 90 kJ/m² | ||
| Thermal | Nominal Value | Test Method |
| Dry: Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa | 220 °C 200 °C | ISO 75-2/B ISO 75-2/A |
| Dry: Melting Temperature(10 °C/min) | 220 °C | ISO 11357-3 |
| Dry: CLTE, Flow | 2.0E-5 cm/cm/°C | ISO 11359-2 |
| Dry: CLTE, Transverse | 7.0E-5 cm/cm/°C | ISO 11359-2 |
| Dry: Flammability Classification(1.6 mm) | HB | IEC 60695-11-10, - 20 |
| Electrical | Nominal Value | Test Method |
| Condition: Surface resistivity | 1.0E+13 ohms | IEC 60093 |
| Dry: Volume Resistivity | > 1.0E+15 Ohms·cm | IEC 60093 |
| Condition: Volume resistivity | 1.0e+14 ohms·cm | IEC 60093 |
| Dry: Relative permittivity 100 Hz 1000000 Hz | 3.50 3.30 | IEC 60250 |
| Condition: Relative Permittivity 100 Hz 1000000 Hz | 14.0 5.00 | IEC 60250 |
| Dry: Dissipation Factor 100 Hz 1000000 Hz | 5.0E-3 0.015 | IEC 60250 |
| Condition: Dissipation factor 100 Hz 1000000 Hz | 0.30 0.12 | IEC 60250 |
| Condition: Comparative Tracking Index | 500 V | IEC 60112 |