https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.htmlMiramid® VE15C is a Polyamide 6 (Nylon 6) material filled with 15% glass fiber. It is available in Europe for injection molding. Important attributes of Miramid® VE15C are: Chemical Resistant Crystalline Fast Molding Cycle Good Stiffness Mold Release Agent Typical applications include: Automotive Engineering/Industrial Parts Coating Applications Construction Applications Electrical/Electronic Applications
| Product Description | |||||
| Miramid® VE15C is a Polyamide 6 (Nylon 6) material filled with 15% glass fiber. It is available in Europe for injection molding. Important attributes of Miramid® VE15C are: Chemical Resistant Crystalline Fast Molding Cycle Good Stiffness Mold Release Agent Typical applications include: Automotive Engineering/Industrial Parts Coating Applications Construction Applications Electrical/Electronic Applications | |||||
| General | |||||
| Form | Resin Pellets | ||||
| Filler | 15 % Glass Fiber | ||||
Feature | Excellent Processability Crystalline Enhanced Stiffness Grease Resistant Solvent Resistant Good Stability | Fuel Resistant High Mechanical Strength And Rigidity | |||
| Building Materials Engineering Parts Sporting Goods | |||||
| Uses | Automotive Protective Covering Electrical | ||||
| Mechanical Parts | |||||
| Physical | Nominal Value | Test Method | |||
| Dry: Density | 1.23 g/cm³ | ISO 1183 | |||
| Dry: Water Absorption, Saturation | 8.5 % | ISO 62 | |||
| Dry: Water Absorption, Equilibrium | 2.0 % | ISO 62 | |||
| Dry: Viscosity Number | 145 cm³/g | ISO 307;ISO 1628;ISO 1157 | |||
| Dry: Tensile Modulus | 5500 MPa | ISO 527-2 | |||
| Condition: Tensile Modulus | 3200 MPa | ISO 527-2 | |||
| Dry: Tensile Stress, Break | 125 MPa | ISO 527-2 | |||
| Condition: Tensile Stress, Break | 75.0 MPa | ISO 527-2 | |||
| Dry: Tensile Strain, Break | 3.0 % | ISO 527-2 | |||
| Condition: Tensile Strain, Break | 11 % | ISO 527-2 | |||
| Dry: Flexural Modulus | 190 MPa | ISO 178 | |||
| Condition: Flexural Modulus | 100 MPa | ISO 178 | |||
| Dry: Charpy Notched Impact Strength -30 °C 23 °C | 6.00 kJ/m² 7.00 kJ/m² | ISO 179 1eA | |||
| Condition: Charpy Notched Impact Strength(23 °C) | 11.0 kJ/m² | ISO 179 1eA | |||
| Dry: Charpy Impact Strength -30 °C 23 °C | 35.0 kJ/m² 45.0 kJ/m² | ISO 179 1eU | |||
| Condition: Charpy Impact Strength(23 °C) | 100 kJ/m² | ISO 179 1eU | |||
| Thermal | Nominal Value | Test Method | |||
| Dry: Deflection Temperature Under Load 0.45 MPa 1.8 MPa | 210 °C 190 °C | ISO 75-2 | |||
| Dry: Melting Temperature, DSC | 220 °C | ISO 3146 | |||
| Electrical | Nominal Value | Test Method | |||
| Dry: Volume Resistivity | 1E+11 ohms·cm | IEC 60093 | |||
| Condition: Volume resistivity | 1E+8 ohms·cm | IEC 60093 | |||
| Dry: Dielectric Constant(1000000 Hz) | 3.50 | IEC 60250 | |||
| Condition: Dielectric Constant(1000000 Hz) | 6.00 | IEC 60250 | |||
| Dry: Dissipation Factor(1000000 Hz) | 0.020 | IEC 60250 | |||
| Condition: Dissipation factor(1000000 Hz) | 0.25 | IEC 60250 | |||
| Dry: Comparative Tracking Index | 550 | IEC 60112 | |||
| Processing | Nominal Value | ||||
| Processing Temp, Melt<Injection> | 260 - 280 °C | ||||
| Mold Temperature<Injection> | 80 - 100 °C | ||||