2-part PU potting sealant
SP297
SP291LV (Low viscosity)
SP297 is a solvent-free, high-performance two-component polyurethane encapsulant. The resin part
(component A) contains hydroxyl groups, and the curing agent (component B) is based on isocyanate.
After mixing A and B, it is cured to form an elastomer. The volume did not change significantly.
It can be cured between 15-65 degrees without bubbles, high volume resistivity, flame retardant grade
UL94 V-0 and other characteristics.
SPECIAL CHARACTERISTICS
- High Performance
- Excellent Chemical Resistance
- Excellent Electrical Properties
- UL91 V-0
- Super Volume Resistivity
- Shore A 85
- Excellent Thermal Conductivity
APPLICATION EXAMPLES
1. Filling coating casting, metal and plastic bonding well;
2. Casting of communication supplies, transformers, electrical and electronic equipment;
3. Filling and sealing of charging pile
| PROPERTY | STANDARD | UNITS | VALUE-SP297 |
| Component | - | -- | Part A | Part B |
| Appearance | Visual | | Black liquid | Dark brown liquid |
| Viscosity | GB/T 10247-2008 | mPa.s | 7500±1500 | 200±50 |
| Density | GB/T 13354-92 | g/cm^3 | 1.5±0.05 | 1.2±0.05 |
| Data details after mixing |
| Mixture ratio | - | Mass ratio | A:B=100:15 |
| Mixing viscosity | GB/T 10247-2008 | mPa.s | 2000±500 |
| Solid content | GB-T 2793-1995 | % | >99 |
| Operation time after mixing | GB/T 10247-2008 | min | 25±5 |
| Tack free time | | Min 25ºC/50% | 50±10 |
| Gel time | GB/T 10247-2008 | Min 25ºC/50% | 40 |
| Curing speed | GB/T 10247-2008 | 100g (plastic cup) /65 ºC | 30min |
| Hardness | GB/T 531.1-2008 | Shore A | 85±5 |
| Tensile strength | GB/T 528-2009 | Mpa | >4 |
| Flame retardant grade | ANSI/UL-94-1985 | UL94 | V-0 |
| Thermal conductivity | GB/T 10297-1998 | W/m.k | 0.64 |
| Elongation at break | GB/T 528-2009 > | % | ≥60 |
| CTI value | GB/T 4207-2012 | - | ≥600 |
| Dielectric strength | GB/T 1693-2007 | kV / mm | > 20 |
| Dielectric constant | GB/T 1693-2007 | - | 4.64 |
| Dielectric loss coefficient 100kHz | GB/T 1693-2007 | 100kHz | 0.1 |
| Volume resistivity | GB/T 1692-92 | Ω • cm | 3.7 ×1015 |
| Water absorption | GB/T 8810-2005 | 24h, 25 ºC,% | 24h/23ºC 0.12%
10d/23ºC 0.21%
0.5h/100ºC 0.09% |
| Application temperature | GB/T 8810-2005 | ºC | -50-150ºC |
Shanghai Sepna Chemical Technology Co., Ltd is special for Polyurethane sealant MS polymer adhesive sealant for automotive glass, bus, and construction joint sealing, bonding. We have been 10+ years in this industry, acquired Switzerland PUNADE in 2005, as the leader of odorless technology in China. With Suzhou, Shanghai has two R&D bases.
At the same time. we have established an excellent sales service team and cooperated with the leading industry of VW, Volvo, Mercedes, Brilliance, Etc. Sepna's products have been widely used in the international market, mainly in North America, South America, Asia, Southeast Asia Middle East and Oceania, etc. Until now, she has serviced nearly 1000 enterprises all over the world.
APPLICATION SOLUTIONS:
1. Windshield sealant- SP86x
2. Automotive adhesive sealant-
-PU structural adhesive
-MS adhesive sealant
3. Electronic potting sealant
4. Powder coating sealant
5. Window & Door corner adhesive
6. Waterproofing coating
7. Expansion joint sealant
- Self-leveling sealant
- Paste sealant
Part B: 6kg/pail
Mixing ratio: 100:15 by weight 1.Delivery time ? Normally, delivery time of sample order is 3 to 7 days, standard order is 7-20 days.
2.How to get free samples ?
Contact with us to get free samples
3.How to be Sepna's distributor ?
As the growing of Sepna's global business,we need to find more and more distributors and agents worldwide. Sepna will provide the best solution and service for our partners. For more information, pls contact with us directly
4.Any OEM/ODM service ?
Sepna can offer the customer OEM label service,and will give the protection of the your right in your market.
Complaint