1.Product Description
Polyamide(PA) are also commonly known as Nylon, the most common types of polyamides are PA6 and PA66, which are characterized by balanced mechanical, electrical and tribological properties. Nylons are often material of choice when it comes to applications that require high strength, rigidity and flame retardant ability.
Properties:
High strength,
High rigidity,
Good heat resistance,
Low water absorption,
Low shrinkage,
Self-lubricating properties, and
Good processing properties
2.The technical parameters
PA66 Technical Date sheet | |||
Properties | Test Method | Units | Value |
Physical property | |||
Specific gravity | ISO1183 | g/cm3 | 1.14 |
Water absorption(23ºC,24hr) | ISO62 | % | 0.2 |
Mechanical properties | |||
Tensile strength at break | ISO527 | MPa | 75 |
Elongation at break | ISO527 | % | 40.3 |
Flexural strength | ISO178 | MPa | 97 |
Flexural modulus | ISO178 | MPa | 2600 |
Charpy impact strength(notched)+23ºC | ISO179(1eA) | KJ/M2 | 6 |
Thermal properties | |||
Deflection temperature at 1.8MPa | ISO75-2 | ºC | 187 |
Melting temperature | ISO11357-1/-3 | ºC | 260 |
Flammability | |||
Flammability | UL94 | V-2 |
HANDAN SHIBO PA66 GF-30 Technical Date sheet | |||
Properties | Test Method | Units | Value |
Physical property | |||
Density | ISO1183 | g/cm3 | 1.36 |
Water absorption(23ºC,24hr) | ISO62 | % | 6 |
Moistrue absorption | 1.6 | ||
Mechanical properties | |||
Tensile Modulus | ISO527-1/-2 | MPa | 11000 |
Tensile strength at break | ISO527-1/-2 | MPa | 205/125 |
Elongation at break | ISO527-1/-2 | % | 3.6/6 |
Flexural strength | ISO178 | MPa | 295/200 |
Flexural modulus | ISO178 | MPa | 3350 |
Charpy impact strength(notched)+23ºC | ISO179(1eA) | KJ/M2 | 10/13 |
Thermal properties | |||
Deflection temperature at 1.8MPa | ISO75-2 | ºC | 250 |
Deflection temperature at 0.45MPa | ISO75-2 | ºC | 260 |
Melting temperature | ISO11357-1/-3 | ºC | 260 |
Flammability | |||
Flammability | UL94 | V-0 | |
HANDAN SHIBO PA6 GF-30 Technical Date sheet | |||
Properties | Test Method | Units | Value |
Physical property | |||
Density | ISO1183 | g/cm3 | 1.35 |
Water absorption(23ºC,24hr) | ISO62 | % | 6.3 |
Moistrue absorption | 1.9 | ||
Mechanical properties | |||
Tensile Modulus | ISO527-1/-2 | MPa | 9500/6000 |
Tensile strength at break | ISO527-1/-2 | MPa | 180/110 |
Elongation at break | ISO527-1/-2 | % | 3.5/7 |
Flexural strength | ISO178 | MPa | 235/ |
Flexural modulus | ISO178 | MPa | 8600 |
Charpy impact strength(notched)+23ºC | ISO179(1eA) | KJ/M2 | 12/25 |
Thermal properties | |||
Deflection temperature at 1.8MPa | ISO75-2 | ºC | 207 |
Deflection temperature at 0.45MPa | ISO75-2 | ºC | 220 |
Melting temperature | ISO11357-1/-3 | ºC | 220 |
Flammability | |||
Flammability | UL94 | HB |