HDPE
High density Polyethylene (HDPE): is a highly crystalline non-polar thermoplastic resin produced through the copolymerization of ethylene and a small amount of α-olefin monomer. HDPE is synthesized under low pressure and is therefore also called low-pressure polyethylene. HDPE is mainly a linear molecular structure and has little branching. It has a high degree of crystallization and high density. It can withstand high temperatures and has good rigidity and mechanical strength and anti-chemical corrosion.
Properties:
High density polyethylene for non-toxic, tasteless, no smelly white particles, melting point is about 130 ° C, relative density of
0.941 ~ 0.960. It has good heat resistance and cold resistance, chemical stability, but also has high rigidity and toughness, good
mechanical strength. Dielectric properties, environmental stress cracking resistance sex also is good.
2.The technical parameters
| Item | Test condition | Test Method | Value | Unit |
| Density | ISO 1183 | 0.944-0.955 | g/cm3 | |
| MFR | 190°C/2.16kg | ISO 1133 | 0.03-0.07 | g/10min |
| Tensile strength at yield | ISO 527-2 | 22 | MPa | |
| Elongation at break | ISO 527-2 | >350 | % | |
| ESCR | F50,50°C,100% | ASTM D-1693A | 1000 | h |
| VICAT | ASTM D-1525 | 126 | °C |
| Item | Test Condition | Test Method | Value | Unit |
| Density | ISO 1183 | 0.950~0.955 | g/cm | |
| MFR | 190°C/2.16kg | ISO 1133 | 1.7~2.5 | g/10min |
| Tensile strength at yield | ISO 527-2 | 24 | MPa | |
| Elongation at break | ISO 527-2 | >600 | % |
| Item | Test Condition | Test Method | Value | Unit |
| MFR | 190°C/2.16kg | ASTM D-1238 | 20 | g/10min |
| Density | --- | ASTM D-792 | 0.954 | g/cm3 |
| Tensile strength at yiled | --- | ASTM D-638 | 28 | MPa |
| Elongation at break | --- | ASTM D-638 | 250 | % |
| Impact tensile strength | --- | ASTM D-1822 | 42 | kJ/m2 |
| ESCR | ASTM D-1693 | 3 | --- | |
| VACIT | --- | ASTM D-1525 | 127 | °C |