| Classification: General grade. Characteristic: super high strength ,high chemical resistance Application: ABS Compounding, disposable lighter, pounding, Electrical &electronic parts,&etc | |||
| General | |||
| Form Resin Pellets | |||
| Feature Chemical Resistant | |||
| Uses Compounding | Electrical | ||
| Physical | Nominal Value | Test Method | |
| Density / Specific Gravity | 1.04 g/cm³ | ASTM D792 | |
| Melt Mass-Flow Rate, MFR(220 °C;10 kg) | 3.0 - 7.0 g/10min | ASTM D1238 | |
| Molding Shrinkage, Flow | 0.20 - 0.60 % | ASTM D955 | |
| Water Absorption(24 hr) | 0.30 % | ASTM D570 | |
| Rockwell Hardness, M-Scale | > 90 | ASTM D785 | |
| Mechanical | Nominal Value | Test Method | |
| Tensile Strength, Yield(50 mm/min;23 °C) | > 78.5 MPa | ASTM D638 | |
| Flexural Modulus(2.8 mm/min;23 °C) | > 3240 MPa | ASTM D790 | |
| Flexural Strength(2.8 mm/min;23 °C) | > 123 MPa | ASTM D790 | |
| Notched Izod Impact Strength(6.4 mm) | > 2.5 kJ/m² | ASTM D256 | |
| Thermal | Nominal Value | Test Method | |
| Deflection Temperature Under Load, Unannealed(1.8 MPa) | > 90.0 °C | ASTM D648 | |
| Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | > 99.0 °C | ASTM D1525 | |
| Flame Rating(3.2 mm) | HB | UL 94 | |
| Processing | Nominal Value | ||
| Drying Temperature<Injection> | 80 - 85 °C | ||
| Drying Time<Injection> | 3.0 hr | ||
| Suggested Max Moisture<Injection> | < 0.10 % | ||
| Rear Temperature<Injection> | 190 - 200 °C | ||
| Middle Temperature<injection> | 200 - 220 °C | ||
| Front Temperature<Injection> | 210 - 220 °C | ||
| Nozzle Temperature<Injection> | 215 - 225 °C | ||
| Processing Temp, Melt<Injection> | 230 °C | ||
| Mold Temperature<Injection> | 60 - 80 °C | ||
| Injection Rate<Injection> | Slow-Moderate | ||